Plenco 07591 (Transfer)
| Category: | Phenolic , Phenolic |
| Manufacturer: | Plastics Engineering Co. |
| Trademark: | Plenco |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mzYeAY_Plenco-07591-Transfer-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PLENCO 07591 is a mineral and flock cotton filled novolac phenolic molding compound. UL recognized under component file E40654. 075914 is available in black. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.46 | g/cm³ | ASTM D792 |
| Apparent Density | 0.61 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow | 0.57 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.18 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (E-Scale) | 77 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8400 | MPa | ASTM D638 |
| Tensile Strength | 37.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 0.50 | % | ASTM D638 |
| Flexural Modulus | 7510 | MPa | ASTM D790 |
| Flexural Strength | 74.5 | MPa | ASTM D790 |
| Compressive Strength | 175 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 30.6 | J/m | ASTM D256 |
| Notched Izod Impact | 31 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 178 | °C | ASTM D648 |
| Continuous Use Temperature | 190 | °C | ASTM D794 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 3.6E+10 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 6.3 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 5.90 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.071 | ASTM D150 | |
| Arc Resistance | 179 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 175 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (4.30 mm) | V-0 | UL 94 | |
| Oxygen Index | 33 | % | ASTM D2863 |
| Additional Information |
|---|
| The value listed as Comparative Tracking Index, UL 746 was tested according to ASTM D3638.The value listed as Mold Shrink, Linear-Flow, ASTM D955 was tested according to the ASTM D6289 standard.Post Shrinkage, ASTM D6289, 72hr, 120°C: 0.29%Drop Ball Impact, PLENCO Method: 150 J/m |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 165 - 182 | °C | |
| Back Pressure | 0.300 | MPa | |
| Screw Speed | < 60 | rpm |
| Injection instructions |
|---|
| Transfer Time: 3-8 secTransfer Pressure: 5.5-6.9 MPaPreheating Temperature: 104-115°C |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TPC PVC SG760 | Thai Plastics and Chemicals Public Company Limited | PVC Homopolymer | TPC PVC |
| Elastron® G G300.D65.N | Elastron USA, Inc. | SEBS | Elastron® G |
| Kumho SBR 1507H | Korea Kumho Petrochemical Co., Ltd. | SBR, Emulsion | Kumho SBR |
| INEOS HDPE A4040 | INEOS Olefins & Polymers USA | HDPE Copolymer | INEOS HDPE |
| Polifor® E 16 TR/10 NATURALE | SO.F.TER. SPA | PP Copolymer | Polifor® |