ENGAGE™ 8842
| Category: | TPO (POE) , Polyolefin Elastomer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ENGAGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WODwUk_ENGAGE-8842.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ENGAGE™ 8842 Polyolefin Elastomer is an ultra-low density ethylene-octene copolymer which offers exceptional properties of an ultra-low density elastomer with the added potential of handling this polymer in pellet form. ENGAGE 8842 has excellent flow characteristics and provides superb impact properties in blends with polypropylene (PP) and polyethylene (PE). It performs well in TPO applications where superior low temperature impact properties are desired. Main Characteristics:
Applications:
|
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.857 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Mooney Viscosity (ML 1+4, 121°C) | 25 | MU | ASTM D1646 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A, 1 sec, Compression Molded | 54 | ||
| Shore D, 1 sec, Compression Molded | 11 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 100% Secant 1(Compression Molded) | 1.40 | MPa | ASTM D638 |
| Tensile Strength 2(Break, Compression Molded) | 3.00 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, Compression Molded) | 1200 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% Secant : Compression Molded | 4.50 | MPa | |
| 2% Secant : Compression Molded | 4.00 | MPa |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 4 | 25.4 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -58.0 | °C | Internal Method |
| Melting Temperature (DSC) 5 | 38.0 | °C | Internal Method |
| Peak Crystallization Temperature (DSC) | 20.0 | °C | Internal Method |
| Note Message | |
|---|---|
| 1 . | 510 mm/min |
| 2 . | 510 mm/min |
| 3 . | 510 mm/min |
| 4 . | Die C |
| 5 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNO ABS R5601A | Techno Polymer America, Inc. | PC+ABS | TECHNO ABS |
| Chemlon® 102 | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| Cri-Line HFLT-615 | Cri-Tech, Inc. | Fluorelastomer | Cri-Line |
| Sylvin 3210-80HMW Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| NORYL GTX™ GTX674PC resin | SABIC Innovative Plastics | PPE+PS+Nylon | NORYL GTX™ |