CABELEC® CA6114
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Cabot Corporation |
| Trademark: | CABELEC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mgvKCn_CABELEC-CA6114.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CABELEC® 6114 is an electrically conductive compound based on conductive carbon black dispersed in a modified high density polyethylene resin. Its electrical and mechanical properties are permanent and are not dependent on atmospheric conditions. APPLICATIONS: CABELEC® 6114 is used for injection moulding applications. It is recommended for product handling applications where freedom from the hazard of electrostatic discharge is necessary. Examples are parts for use in automotive fuel systems or where there is handling of explosive powders and liquids, pigments or electronic components. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.07 | g/cm³ | Internal Method |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/10.0 kg | 4.5 | g/10 min | |
| 190°C/21.6 kg | 16 | g/10 min | |
| 190°C/5.0 kg | 1.0 | g/10 min | |
| Molding Shrinkage - Flow | 2.5 to 3.5 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 61 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 649 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 22.0 | MPa | |
| Break | 18.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 19 | % | |
| Break | 150 | % | |
| Flexural Modulus | 744 | MPa | ISO 178 |
| Flexural Stress | 23.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 20 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 65.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 40.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 119 | °C | ISO 306/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.6E+2 | ohms | Internal Method |
| Volume Resistivity | 20 | ohms·cm | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 190 | °C | |
| Middle Temperature | 190 | °C | |
| Front Temperature | 190 | °C | |
| Nozzle Temperature | 215 | °C | |
| Mold Temperature | 35.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ming Dih EPS S2-211 | Ming Dih Group Corporation | PS (EPS) | Ming Dih EPS |
| Wondel® T TG3 | Nanjing Julong Engineering Plastics Co., LTD | PBT | Wondel® T |
| Varcum 29538 | Durez Corporation | Phenolic | Varcum |
| ACCUTECH™ CP0437M20CL | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| IDI BMC B30 (Glass Content 20%) | IDI Composites International | TS, Unspecified | IDI BMC |