ENGAGE™ 8200
| Category: | TPO (POE) , Polyolefin Elastomer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ENGAGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mgEAGT_ENGAGE-8200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ENGAGE™ 8200 Polyolefin Elastomer is an ethylene-octene copolymer that has excellent flow characteristics and performs well in a wide range of general purpose thermoplastic elastomer applications. ENGAGE 8200 provides superb impact properties in blends with polypropylene (PP) and polyethylene (PE), especially in applications requiring slightly higher melt flow. ENGAGE 8200 also provides high filler loading capability, excellent electrical properties, and (when cross-linked) exceptional heat aging, compression set, and weather resistance properties. Main Characteristics:
Applications:
|
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.870 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 5.0 | g/10 min | ASTM D1238 |
| Mooney Viscosity (ML 1+4, 121°C) | 8 | MU | ASTM D1646 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A, 1 sec, Compression Molded | 66 | ||
| Shore D, 1 sec, Compression Molded | 17 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 100% Secant 1(Compression Molded) | 2.30 | MPa | ASTM D638 |
| Tensile Strength 2(Break, Compression Molded) | 5.70 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, Compression Molded) | 1100 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% Secant : Compression Molded | 10.9 | MPa | |
| 2% Secant : Compression Molded | 10.8 | MPa |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 4 | 37.1 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -53.0 | °C | Internal Method |
| Vicat Softening Temperature | 37.0 | °C | ASTM D1525 |
| Melting Temperature (DSC) 5 | 59.0 | °C | Internal Method |
| Peak Crystallization Temperature (DSC) | 44.0 | °C | Internal Method |
| Note Message | |
|---|---|
| 1 . | 510 mm/min |
| 2 . | 510 mm/min |
| 3 . | 510 mm/min |
| 4 . | Die C |
| 5 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Milastomer™ M2400BS | Mitsui Chemicals America, Inc. | TPV | Milastomer™ |
| AZDEL™ R401-B01 | Azdel, Inc. | PP, Unspecified | AZDEL™ |
| APEX® 3201-75NT | Teknor Apex Company | PVC, Flexible | APEX® |
| INEOS PP H03W-01 | INEOS Olefins & Polymers USA | PP Homopolymer | INEOS PP |
| SD POLYCA™ CF5201V | Sumika Styron Polycarbonate Limited | PC | SD POLYCA™ |