OmniTech™ HDPE GRC40
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | OMNI Plastics, LLC |
| Trademark: | OmniTech™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mbDHg3_OmniTech-HDPE-GRC40.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| OmniTech™ HDPE GRC40 is a High Density Polyethylene product filled with 40% glass fiber. It can be processed by injection molding and is available in North America. Primary characteristic: chemically coupled. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.26 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 66.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 6720 | MPa | ASTM D790 |
| Flexural Strength (Break) | 100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 130 | J/m | ASTM D256 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 204 to 249 | °C | |
| Middle Temperature | 204 to 249 | °C | |
| Front Temperature | 204 to 249 | °C | |
| Nozzle Temperature | 204 to 249 | °C | |
| Processing (Melt) Temp | 204 to 249 | °C | |
| Mold Temperature | 26.7 to 82.2 | °C | |
| Back Pressure | 0.345 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SPI 1029 NAT | Service Polymers, Inc. | Nylon 6 | SPI |
| Yanshan PE 8300B | SINOPEC Beijing Yanshan Petrochemical | HDPE | Yanshan PE |
| Adiprene® LF 1700A | Chemtura | PUR-Ester/TDI | Adiprene® |
| Lutene® H BE0350 | LG Chem Ltd. | HDPE | Lutene® H |
| MAJORIS FTR212 - 8229 | AD majoris | PP, Unspecified | MAJORIS |