Stylac™ 783
| Category: | AS , Acrylonitrile Styrene Copolymer |
| Manufacturer: | Asahi Kasei Chemicals Corporation |
| Trademark: | Stylac™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | maHmeP_Stylac-783.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Stylac™ 783 is an Acrylonitrile Styrene Copolymer (AS) product. It is available in Africa & Middle East, Asia Pacific, or Europe. Typical application: Food Contact Applications. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.08 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 9.0 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 9.54 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow | 0.40 to 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 73.7 | MPa | ISO 527-2/5 |
| Flexural Modulus 1 | 3750 | MPa | ISO 178 |
| Flexural Stress 2 | 139 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 1.3 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 89.3 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 105 | °C | ISO 306/B |
| RTI Elec | 50.0 | °C | UL 746 |
| RTI Imp | 50.0 | °C | UL 746 |
| RTI Str | 50.0 | °C | UL 746 |
| Ball Pressure Test 3 | 95 | °C | EMAC |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Registered Number: B-1573 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-fax 6431 | INDELPRO, S.A. de C.V. | PP Homopolymer | Pro-fax |
| TAROLOX 10 G4 DX03 | Taro Plast S.p.A. | PBT | TAROLOX |
| DINAPLEN® PPH1S25 C20-4152 | Grupo Repol | PP Homopolymer | DINAPLEN® |
| LG EPS R240 | LG Chem Ltd. | PS (EPS) | LG EPS |
| Sylvin 9993-65 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |