Resinol PP Type O
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Spartech Plastics |
| Trademark: | RESINOL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mQ6wev_Resinol-PP-Type-O.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Resinol PP Type O is a polypropylene product,. It is available in North America. The application areas of Resinol PP Type O include cans, sporting goods and medical/health care. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.903 | g/cm³ | ASTM D792 |
| -- | 0.905 | g/cm³ | ASTM D1505 |
| Environmental Stress-Cracking Resistance | 325 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 85 | ASTM D785 | |
| Durometer Hardness (Shore D) | 68 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1240 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 22.1 | MPa | ASTM D638 |
| -- 1 | 30.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Yield) | 6.5 | % | ASTM D638 |
| Compressive Strength | 41.4 | MPa | ASTM D695 |
| Deformation Under Load (50°C, 14 MPa) | 1.00 | % | ASTM D621 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -18°C | 18 | J/m | ASTM D256 |
| 23°C | 56 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 4300 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 102 | °C | ASTM D648 |
| Brittleness Temperature | -28.9 | °C | ASTM D746 |
| Vicat Softening Temperature | 167 | °C | ASTM D1525 |
| CLTE - Flow | 1.0E-4 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 6.5E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 24 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 2.20 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 3.0E-4 | ASTM D150 |
| Additional Information |
|---|
| Density, ASTM D1505: 0.9 to 0.91g/ccTensile Strength, ASTM 638, .2in/min: 3200 to 5300psiNotched Izod Impact Strength, ASTM D256, 73°F (23°C): .8 to 1.3 ft-lb/inBrittleness Temperature, ASTM D746: -20°F to 32°FHardness, Shore D: 55-70Modulus of Elasticity, ASTM D638: 180000 to 190000 psiCompressive Stress, ASTM D695: 5500 to 6500 psiElongation, ASTM D638, .2in/min:128-860%Volume Resistivity: >6.5E15 ohm-cmDielectric Strength, ASTM D149, step by step, 1/8in: 650 volts/milDielectric Constant, ASTM D150, 1E6 cycles: 2.1 to 2.3 volts/mil |
| Note Message | |
|---|---|
| 1 . | 5.1 mm/min |
| 2 . | 5.1 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Romiloy® 1015/01 F | ROMIRA GmbH | PC+ABS | Romiloy® |
| RAYPRENE® NB221-S4086 | R&P (Pte.) Ltd. | TPE | RAYPRENE® |
| Sylvin 8245-75 White 1586 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Kanghui KH2100 | Yingkou Kanghui Petrochemical Co., LTD. | PBT | Kanghui |
| XYLEX™ X7507 resin | SABIC Innovative Plastics | PC+Polyester | XYLEX™ |