AFR067 is a halogen free flame retardant compound UL 94 V2, intended for extrusion and profiles. The product is available in natural but other colours can be provided on request AFR067 produce very low level of toxicity and low smoke density in the case of a fire. This quality is UV stabilised. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.980 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.70 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.6 to 1.7 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1700 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 18.0 | MPa | |
| Break | 25.0 | MPa | |
| Tensile Strain (Yield) | 6.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 1400 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 100 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 75.0 | °C | ISO 75-2/A |
| Ball Pressure Test (125°C) | Pass | NF C 61-303 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | V-2 | ||
| 1.60 mm | V-2 | ||
| 3.20 mm | V-0 | ||
| Glow Wire Flammability Index (2.00 mm) | 960 850 | °C | IEC 60695-2-12 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Cylinder Zone 1 Temp. | 180 to 190 | °C | |
| Cylinder Zone 3 Temp. | 180 to 190 | °C | |
| Cylinder Zone 5 Temp. | 180 to 190 | °C | |
| Melt Temperature | 200 | °C | |
| Head Temperature | 200 | °C | |
| Die Temperature | 200 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marvel™ M10 | SCG Chemicals Co., Ltd. | LLDPE | Marvel™ |
| NuSil MED-4755 | NuSil Technology | Rubber | NuSil |
| Jam PE 23507 | Jam Petrochemical Company | LLDPE | Jam PE |
| Lupol® TE5109 | LG Chem Ltd. | PP, Unspecified | Lupol® |
| Plexiglas® VS-UVT | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Plexiglas® |