FRblend® PA6-1301
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Colour Image Plastic Compound Sdn. Bhd. (CIPC) |
| Trademark: | FRblend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mGaLVK_FRblend-PA6-1301.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FRblend® PA6-1301 is mineral and glass fiber reinforced, flame retardant polyamide compound. This grade offers excellent flame retardancy with balanced mechanical properties and heat resistance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.59 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 1.0 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.4 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8300 | MPa | ASTM D638 |
| Tensile Strength | 85.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus | 7100 | MPa | ASTM D790 |
| Flexural Strength | 129 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 87 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 4.00 mm) | 169 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 220 to 230 | °C | |
| Middle Temperature | 230 to 240 | °C | |
| Front Temperature | 240 to 250 | °C | |
| Nozzle Temperature | 250 to 260 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 209E | RTP Company | Nylon, Unspecified | RTP |
| Compoceran E201 | Arakawa Chemical Industries, Ltd. | Epoxy | Compoceran |
| HiFill® PA6/6 CM40 6122 BK | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| Hostacom CR 1171 G1 | LyondellBasell Industries | PP Impact Copolymer | Hostacom |
| RTP 199 X 143528 | RTP Company | PP, Unspecified | RTP |