VALOX™ 420SE0 resin
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6RXDRm_VALOX420SE0resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% glass reinforced, UL94 V-0/5V rated. Numerous applications: edge trimmers, food mixer motor stator and commutator, cooling fan, connectors, bobbins, switches etc |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.63 | g/cm³ | ASTM D792, ISO 1183 |
| Specific Volume | 0.610 | cm³/g | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/5.0 kg) | 42 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (250°C/5.0 kg) | 29.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Flow 1 | 0.10 - 0.50 | % | Internal method |
| Flow : 3.20mm | 0.50 - 0.70 | % | Internal method |
| Transverse flow 2 | 0.40 - 0.80 | % | Internal method |
| Transverse flow : 3.20mm | 0.50 - 1.0 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.090 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.070 | % | ISO 62 |
| Outdoor Suitability | f2 | UL 746C |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 119 | ASTM D785 | |
| R scale | 119 | ISO 2039-2 | |
| Ball Indentation Hardness (H 358/30) | 118 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 3 | 12000 | MPa | ASTM D638 |
| -- | 10000 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 4 | 120 | MPa | ASTM D638 |
| Yield | 120 | MPa | ISO 527-2/5 |
| Fracture 5 | 120 | MPa | ASTM D638 |
| Fracture | 120 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 6 | 2.0 | % | ASTM D638 |
| Yield | 1.9 | % | ISO 527-2/5 |
| Fracture 7 | 2.0 | % | ASTM D638 |
| Fracture | 1.9 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 8 | 9800 | MPa | ASTM D790 |
| -- 9 | 9500 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 180 | MPa | ISO 178 |
| Fracture, 50.0mm span 10 | 186 | MPa | ASTM D790 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 22.0 | mg | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 11 | ISO 179/1eA | ||
| -30°C | 6.0 | kJ/m² | ISO 179/1eA |
| 23°C | 7.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 12 | ISO 179/1eU | ||
| -30°C | 50 | kJ/m² | ISO 179/1eU |
| 23°C | 50 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | |||
| -30°C | 57 | J/m | ASTM D256 |
| 23°C | 60 | J/m | ASTM D256 |
| -30°C 13 | 6.0 | kJ/m² | ISO 180/1A |
| 23°C 14 | 7.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 620 | J/m | ASTM D4812 |
| -30°C 15 | 45 | kJ/m² | ISO 180/1U |
| 23°C 16 | 45 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Total Energy) | 5.00 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 212 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 100 mm span 17 | 220 | °C | ISO 75-2/Be |
| 1.8 MPa, unannealed, 3.20mm | 200 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 100 mm span 18 | 195 | °C | ISO 75-2/Ae |
| 1.8 MPa, unannealed, 64.0mm span 19 | 200 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 200 | °C | ASTM D1525, ISO 306/B50, ISO 306/B120 20 |
| -- | 220 | °C | ISO 306/A50 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 2.5E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Flow : 23 to 80°C | 2.5E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 8.9E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : 23 to 80°C | 1.2E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.25 | W/m/K | ISO 8302 |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 130 | °C | UL 746 |
| RTI | 140 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | |||
| 1.60 mm, in Oil | 24 | kV/mm | ASTM D149 |
| 3.20 mm, in Air | 19 | kV/mm | ASTM D149 |
| 0.800mm, in oil | 23 | kV/mm | IEC 60243-1 |
| 1.60mm, in oil | 22 | kV/mm | IEC 60243-1 |
| 3.20mm, in oil | 16 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 100 Hz | 3.80 | ASTM D150, IEC 60250 | |
| 1 MHz | 3.70 | ASTM D150 | |
| 50 Hz | 3.30 | IEC 60250 | |
| 60 Hz | 3.30 | IEC 60250 | |
| 1 MHz | 3.30 | IEC 60250 | |
| Dissipation Factor | |||
| 100 Hz | 2.0E-3 | ASTM D150, IEC 60250 | |
| 1 MHz | 0.020 | ASTM D150 | |
| 50 Hz | 1.0E-3 | IEC 60250 | |
| 60 Hz | 1.0E-3 | IEC 60250 | |
| 1 MHz | 0.010 | IEC 60250 | |
| Arc Resistance 21 | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 | |
| Comparative Tracking Index | IEC 60112 | ||
| -- | 175 | V | IEC 60112 |
| Solution B | 125 | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 4 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 2 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.400 mm | V-2 | UL 94 | |
| 0.710 mm | V-0 | UL 94 | |
| 2.00 mm | 5VA | UL 94 | |
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Oxygen Index | 32 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 12 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 80 | % | |
| Rear Temperature | 243 - 266 | °C | |
| Middle Temperature | 249 - 271 | °C | |
| Front Temperature | 254 - 277 | °C | |
| Nozzle Temperature | 249 - 271 | °C | |
| Processing (Melt) Temp | 254 - 277 | °C | |
| Mold Temperature | 65.6 - 87.8 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 50 - 80 | rpm | |
| Vent Depth | 0.025 - 0.038 | mm |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | Tensile Bar |
| 3 . | 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | Type 1, 5.0 mm/min |
| 7 . | Type 1, 5.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 2.0 mm/min |
| 10 . | 1.3 mm/min |
| 11 . | 80*10*4 sp=62mm |
| 12 . | 80*10*4 sp=62mm |
| 13 . | 80*10*4 |
| 14 . | 80*10*4 |
| 15 . | 80*10*4 |
| 16 . | 80*10*4 |
| 17 . | 120*10*4 mm |
| 18 . | 120*10*4 mm |
| 19 . | 80*10*4 mm |
| 20 . | 标准 B (120°C/h), 载荷2 (50N) |
| 21 . | Tungsten electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SBC3715 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| ADENE BCFB | A.D. Compound spa | PP Homopolymer | ADENE |
| Latishield 66-08A G/25-V0KB1 | LATI S.p.A. | Nylon 66 | Latishield |
| LUVOCOM® 80/TF/18/SI/2/BK | Lehmann & Voss & Co. | Acetal (POM) Copolymer | LUVOCOM® |
| Plaslube® PA6/12 01430 | Techmer Engineered Solutions | Nylon 12 | Plaslube® |