PRE-ELEC® ABS 1410
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Premix Oy |
| Trademark: | PRE-ELEC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lw2lNw_PRE-ELEC-ABS-1410.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRE-ELEC® ABS 1410 is a conductive thermoplastic compound based on ABS. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC® ABS 1410 has excellent mechanical properties and is easy to injection mold. PRE-ELEC® ABS 1410 is intended for injection molding of precise technical parts with good impact strength. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.08 | g/cm³ | ASTM D792 |
| -- | 1.10 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 15 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.50 to 0.80 | % | ASTM D955, ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 76 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Flow : Yield | 35.9 | MPa | ASTM D638 |
| Flow : Yield | 36.0 | MPa | ISO 527-2 |
| Across Flow | 30.0 | MPa | ASTM D638 |
| Flow | 29.0 | MPa | ASTM D638 |
| -- 1 | 30.0 | MPa | ISO 527-2 |
| -- 2 | 29.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Flow : Yield | 4.0 | % | |
| Break 3 | 4.0 | % | |
| Break 4 | 8.0 | % | |
| Flexural Modulus (4.00 mm) | 2000 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -20°C 5 | 21 | kJ/m² | ASTM D256 |
| -20°C 6 | 2.0 | kJ/m² | ISO 179 |
| 23°C 7 | 5.0 | kJ/m² | ISO 179 |
| 23°C 8 | 34 | kJ/m² | ASTM D256 |
| Charpy Unnotched Impact Strength 9 | |||
| -20°C | 21 | kJ/m² | ASTM D256, ISO 179 |
| 23°C | 33 | kJ/m² | ISO 179 |
| 23°C | 34 | kJ/m² | ASTM D256 |
| Notched Izod Impact (Area) | ASTM D256 | ||
| -20°C, 4.00 mm | 4.20 | kJ/m² | |
| 23°C, 4.00 mm | 6.30 | kJ/m² | |
| Notched Izod Impact Strength 10 | ISO 180 | ||
| -20°C | 6.0 | kJ/m² | |
| 23°C | 7.0 | kJ/m² | |
| Unnotched Izod Impact (Area) | ASTM D256 | ||
| -20°C, 4.00 mm | 29.4 | kJ/m² | |
| 23°C, 4.00 mm | 39.9 | kJ/m² | |
| Unnotched Izod Impact Strength 11 | ISO 180 | ||
| -20°C | 30 | kJ/m² | |
| 23°C | 40 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 87.8 | °C | ASTM D648B |
| 0.45 MPa, Unannealed | 88.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 72.8 | °C | ASTM D648A |
| 1.8 MPa, Unannealed | 73.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 104 | °C | ASTM D1525, ISO 306/A50 6 12 |
| -- | 91.1 | °C | ASTM D1525 13 |
| -- | 91.0 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+5 | ohms | IEC 61340-2-3 |
| Volume Resistivity | < 1.0E+5 | ohms·cm | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 220 to 260 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C | |
| Injection Pressure | 75.0 to 120 | MPa | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | Across Flow |
| 2 . | Flow |
| 3 . | Across Flow |
| 4 . | Flow |
| 5 . | 4 mm thickness |
| 6 . | 4 mm thick |
| 7 . | 4 mm thick |
| 8 . | 4 mm thickness |
| 9 . | 4 mm thick |
| 10 . | 4 mm thick |
| 11 . | 4 mm thick |
| 12 . | Rate A (50°C/h), Loading 2 (50 N) |
| 13 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Suprel® SVA 9812 | Axiall Corporation | PVC, Rigid | Suprel® SVA |
| VICTREX® PEEK 380P | Victrex plc | PEEK | VICTREX® PEEK |
| Nordbak Castable Wear Compound | Loctite® | Epoxy | Nordbak |
| Enviramid® N2300STHL BK | Ravago Manufacturing Americas, LLC | Nylon 6 | Enviramid® |
| Hifax TKC 115X Black | LyondellBasell Industries | PP, Unspecified | Hifax |