POLYSTONE® P homopolymer
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Röchling Engineering Plastics SE & Co. KG |
| Trademark: | POLYSTONE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DqDyfS_POLYSTONE-P-homopolymer.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Product characteristics
Typical field of application
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ISO 1183 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | < 0.010 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 72 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1300 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 32.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 50 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 4.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Continuous Use Temperature | |||
| -- 1 | 0.00 to 100 | °C | |
| -- 2 | < 150 | °C | |
| Melting Temperature | 162 to 167 | °C | ISO 11357-3 |
| CLTE - Flow | 1.2E-4 to 1.9E-4 | cm/cm/°C | DIN 53752 |
| Specific Heat | 1700 | J/kg/°C | DIN 52612 |
| Thermal Conductivity | 0.20 | W/m/K | DIN 52612 |
| Heat Deflection Temperature - Vicat B | 90 | °C | ISO 306 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+14 | ohms·cm | IEC 60093 |
| Electric Strength | 45 | kV/mm | IEC 60243-1 |
| Dielectric Constant | 2.40 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 1.9E-4 | IEC 60250 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 3.00 mm | HB | ||
| 6.00 mm | HB |
| Note Message | |
|---|---|
| 1 . | Long Term |
| 2 . | Short Term |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPRAN® LFT PA 1345 | SAMBARK | Nylon 6 | SUPRAN® LFT PA |
| Fainplast PVC GS 69/PL | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| KRYSTALGRAN™ PE399-100 | Huntsman Corporation | PUR-Eth,aliphat | KRYSTALGRAN™ |
| Karina BLACK PVC COMPOUND 70900-48/1-F-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PERLAS® O07F3000B11 | A.D. Compound S.p.A. | PP Copolymer | PERLAS® |