Order Products : sales@su-jiao.com
Eltex® PF6212AA
| Category: | mLLDPE , Metallocene Linear Low Density Polyethylene |
| Manufacturer: | INEOS Olefins & Polymers Europe |
| Trademark: | Eltex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lmnq7G_Eltex-PF6212AA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Eltex® PF6212AA is a metallocene LLDPE grade produced in Europe Benefits & Features Eltex® PF6212AA is a polyethylene copolymer containing hexene-1 as the comonomer produced with a metallocene catalyst. It offers the following properties:
Applications Eltex® PF6212AA has been developed for use in food packaging and other thin film applications where excellent mechanical and optical performance is required. For more demanding applications such as lamination and temporary surface protection, we recommend to use Eltex® PF6212LA If corona treatment is necessary, the level should normally be in the range 38-48 mN/m. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.919 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.3 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| 1% Secant, MD : 25 µm | 180 | MPa | |
| 1% Secant, TD : 25 µm | 200 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 25 µm | 9.00 | MPa | |
| TD : Yield, 25 µm | 10.0 | MPa | |
| MD : Break, 25 µm | 65.0 | MPa | |
| TD : Break, 25 µm | 60.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 25 µm | 550 | % | |
| TD : Break, 25 µm | 670 | % | |
| Dart Drop Impact (25 µm) | > 1000 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm | 200 | g | |
| TD : 25 µm | 440 | g |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature 1 | 105 to 118 | °C | ASTM D3418 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm) | 65 | ASTM D2457 | |
| Haze (25.0 µm) | 7.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | 2nd heating |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1200 S-90A | RTP Company | TPU-Polyester | RTP |
| Ravago Compounds GFP-4413 | Ravago Manufacturing Americas, LLC | PP, Unspecified | Ravago Compounds |
| 4MID® 9B22145 HUVW | 4Plas | Nylon 6 | 4MID® |
| Bormed™ RF830MO | Borealis AG | PP Random Copolymer | Bormed™ |
| SQUARE® LIM1962-50A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |