LNP™ LUBRICOMP™ LL003 compound
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | l9CAAq_LNP-LUBRICOMP-LL003-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP LL003 is a compond based on Polyetheretherketone resin containing 15% PTFE Lubricant. Added feature of this material is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound LL-4030 Product reorder name: LL003 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.39 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.90 to 2.0 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.078 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.089 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3010 | MPa | ASTM D638 |
| -- | 3080 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 64.4 | MPa | ASTM D638 |
| Yield | 62.0 | MPa | ISO 527-2/5 |
| Break 3 | 64.4 | MPa | ASTM D638 |
| Break | 62.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 4.6 | % | ASTM D638 |
| Yield | 3.3 | % | ISO 527-2/5 |
| Break 5 | 4.6 | % | ASTM D638 |
| Break | 3.3 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2940 | MPa | ASTM D790 |
| -- 7 | 2750 | MPa | ISO 178 |
| Flexural Stress | 92.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.43 | ||
| vs. Itself - Static | 0.32 | ||
| Wear Factor - Washer | 18.5 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 48 | J/m | ASTM D256 |
| 23°C 8 | 5.4 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 720 | J/m | ASTM D4812 |
| 23°C 9 | 38 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 3.10 | J | ASTM D3763 |
| -- | 0.800 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 156 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 156 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 146 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 147 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 4.7E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 5.7E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 370 to 380 | °C | |
| Middle Temperature | 380 to 400 | °C | |
| Front Temperature | 380 to 400 | °C | |
| Mold Temperature | 175 to 190 | °C | |
| Back Pressure | 0.300 to 0.700 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMOFIN PPH308G50 | Polyram Ram-On Industries | PP Homopolymer | RAMOFIN |
| DENIBLEND E | Vamp Tech | PC+ABS | DENIBLEND |
| EMOPLEN® A 750 | EMAS Plastik San.Tic.AS. | PP Copolymer | EMOPLEN® |
| LUVOCOM® 80-8999/BL/L | Lehmann & Voss & Co. | Acetal (POM) Copolymer | LUVOCOM® |
| Optix® CA-41 UVT | Plaskolite, Inc. | Acrylic (PMMA) | Optix® |