LUVOCOM® 1114-0717 Datasheet,PAEK,Lehmann & Voss & Co.-SHANGHAI SUSHENG

Message
LUVOCOM®1114-0717 is a polyaryl ketone (PAEK) material containing a carbon fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. LUVOCOM®The main features of 1114-0717 are: flame retardant/rated flame Conductivity Electrostatic protection Lubrication Typical application areas include: textile/fiber engineering/industrial accessories Aerospace Automotive Industry medical/health care

General Information
Filler / Reinforcement	Carbon fiber reinforced material
Additive	PTFE lubricant
Features	Conductivity Electrostatic discharge protection Lubrication
Uses	Textile applications Engineering accessories Aerospace applications Application in Automobile Field Medical/nursing supplies
Appearance	Dark gray

Physical	Nominal Value	Unit	Test Method
Density	1.51	g/cm³	ISO 1183
Molding Shrinkage	0.10 - 0.30	%	DIN 16901
Water Absorption (23°C, 24 hr)	< 0.10	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	17000	MPa	ISO 527-2
Tensile Stress (Break)	180	MPa	ISO 527-2
Tensile Strain (Yield)	1.5	%	ISO 527-2
Flexural Modulus	14000	MPa	ISO 178
Flexural Stress	240	MPa	ISO 178
Coefficient of Friction
Dynamic	0.19
Static	0.17
Flexural Strain at Flexural Strength	2.0	%	ISO 178

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance		ohms	IEC 60167

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	12	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength			ISO 179/1fU
-30°C	20	kJ/m²	ISO 179/1fU
23°C	25	kJ/m²	ISO 179/1fU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	305	°C	ISO 75-2/A
Continuous Use Temperature	255	°C	UL 746B
Vicat Softening Temperature	320	°C	ISO 306/A
CLTE - Flow	5.0E-6	cm/cm/°C	DIN 53752
Thermal Conductivity	0.60	W/m/K	DIN 52612

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	< 1.0E+4	ohms	IEC 60093

Flammability	Nominal Value	Unit	Test Method
Flame Rating ¹	V-0		UL 94

Injection	Nominal Value	Unit
Drying Temperature
B	120	°C
Hot air dryer, A	150	°C
Drying time- Hot air dryer, A	4.0 - 6.0	hr
Suggested Max Moisture	0.050	%
Rear Temperature	370 - 420	°C
Middle Temperature	380 - 420	°C
Front Temperature	390 - 420	°C
Nozzle Temperature	390 - 420	°C
Processing (Melt) Temp	390	°C
Mold Temperature	160 - 200	°C

Injection instructions
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture content should not exceed 0.05%. To avoid internal stresses, a medium to high injection rate should be used. An increase in tool temperature may be helpful. Post-crystallization may lead to warpage at elevated operating temperatures. This can be counteracted by suitable heat treatment. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. High-temperature polymers place increased demands on the tool steels employed. Please contact us for further information.

Injection instructions

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture content should not exceed 0.05%. To avoid internal stresses, a medium to high injection rate should be used. An increase in tool temperature may be helpful. Post-crystallization may lead to warpage at elevated operating temperatures. This can be counteracted by suitable heat treatment. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. High-temperature polymers place increased demands on the tool steels employed. Please contact us for further information.

Note Message
1 .	Not recognized by UL.

Category:	PAEK , Polyaryletherketone
Manufacturer:	Lehmann & Voss & Co.
Trademark:	LUVOCOM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	kvgBGc_LUVOCOM-1114-0717.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
RTP 1605 TFE 15	RTP Company	PAS	RTP
Sumikon® FM-MK275A	Sumitomo Bakelite Co., Ltd.	PPS	Sumikon®
Alathon® H5618	LyondellBasell Industries	HDPE	Alathon®
ELASTOSIL® RT 708	Wacker Chemie AG	Silicone	ELASTOSIL® RT
OP - PC - Unfilled 68	Oxford Polymers	PC	OP - PC - Unfilled