NORYL GTX™ APS430 resin
| Category: | PPS+PPE , Polyphenylene Sulfide + PPE |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | NORYL GTX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kn2z4I_NORYL-GTX-APS430-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PPE + PPS GF 30%, FR V-0 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.48 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/5.0 kg) | 44 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.30 to 0.70 | % | Internal Method |
| Water Absorption (24 hr) | 0.020 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 123 | MPa | Internal Method |
| Tensile Elongation (Break) | 10 | % | Internal Method |
| Flexural Modulus | 8620 | MPa | ASTM D790 |
| Flexural Strength | 167 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 78 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 255 | °C | ASTM D648 |
| CLTE - Flow (-30 to 30°C) | 1.8E-5 to 5.8E-5 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257 |
| Dielectric Constant | ASTM D150 | ||
| 50 Hz | 3.30 | ||
| 60 Hz | 3.30 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD C 205 A | RTP Company | Nylon 66 | RTP |
| APICAL 120AF616 | Kaneka Corporation | Film, PI | APICAL |
| Flexoprene® 95 | Puma Tecnica S.A.I.C.F.I | PE, Unspecified | Flexoprene® |
| Latishield 73/13-07A | LATI S.p.A. | Acetal (POM) Copolymer | Latishield |
| Karina BEIGE PVC COMPOUND 801-08/ 98-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |