ElectriPlast® EP-SS/PC/ABS
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Integral Technologies, Inc. |
| Trademark: | ElectriPlast® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kgT0GG_ElectriPlast-EP-SS-PC-ABS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ElectriPlast®EP-SS/PC/ABS is a polycarbonate acrylonitrile butadiene styrene (PC ABS) product, which contains stainless steel fiber as filler. It can be processed by injection molding and is available in North America. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.67 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4950 | MPa | ASTM D638 |
| Tensile Strength (Break) | 56.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 4890 | MPa | ASTM D790 |
| Flexural Strength | 102 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 57 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 210 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 99.0 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 23 | ohms | ESD STM11.11 |
| Volume Resistivity | 6.0 | ohms·cm | ASTM D257 |
| Static Decay | 10 | msec | Internal method |
| Surface Resistance | 2.0 | ohms | ESD STM11.11 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (No Burn) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 246 | °C | |
| Middle Temperature | 257 | °C | |
| Front Temperature | 257 | °C | |
| Nozzle Temperature | 268 | °C | |
| Mold Temperature | 65.6 | °C | |
| Back Pressure | 1.72 | MPa | |
| Screw Speed | 75 | rpm |
| Injection instructions |
|---|
| Injection Speed: 1 in/sec1st Stage (injection): 2400 psi2nd Stage (molding): 1200 psiDecomposition: 0.5 inch |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAISOX 8003H | Formosa Plastics Corporation | HDPE | TAISOX |
| Arylmax® K6020GF30 | Polymics, Ltd. | PAEK | Arylmax® |
| Hetron™ FR 998/35 | Ashland Performance Materials | Vinyl Ester | Hetron™ |
| HiFill® PP GF40 | Techmer Engineered Solutions | PP, Unspecified | HiFill® |
| Sumiliteresin® PR-1028 I | SBHPP | Phenolic | Sumiliteresin® |