Order Products : sales@su-jiao.com
WPP PP PPC3TF2-Black
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Washington Penn Plastic Co. Inc. |
| Trademark: | WPP PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kbtx8T_WPP-PP-PPC3TF2-Black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
WPP PP PPC3TF2-Black is a polypropylene copolymer (PP Copoly) product, which contains 20% talc filler. It can be processed by injection molding and is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: automotive industry. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 66 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 28.0 | MPa | ASTM D638 |
| Yield | 29.0 | MPa | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 2 | 2100 | MPa | ASTM D790 |
| -- 3 | 2200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 41 | J/m | ASTM D256 |
| -40°C | 2.0 | kJ/m² | ISO 180 |
| 10°C | 3.5 | kJ/m² | ISO 180 |
| 23°C | 4.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 116 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 66.0 | °C | ASTM D648, ISO 75-2/Af |
| 1.8 MPa, not annealed | 68.0 | °C | ISO 75-2/A |
| Additional Information |
|---|
| Tested at 23 ± 2°C (73.4 ± 3.6°F) and 50 ± 5% relative humidity unless otherwise noted. |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Precision Polymer S70H | Precision Polymer Engineering Ltd. | Silicone | Precision Polymer |
| Daelim Po1y® PA-164V | DAELIM INDUSTRIAL CO., LTD. | PP Homopolymer | Daelim Po1y® |
| Indothene HD 46GP009UV | Reliance Industries Limited | HDPE | Indothene HD |
| Jamplast JPPPO | Jamplast, Inc. | PPE+PS | Jamplast |
| OTECH PVC PL1001-11 - Plenum Insulation | OTECH Corporation | PVC, Unspecified | OTECH PVC |