Karina COMP. PVC IVORY -E 75930-35/ 1-F-AC-HSF
| Category: | PVC, Unspecified , Polyvinyl Chloride |
| Manufacturer: | Karina Ind. e Com. de Plásticos Ltda |
| Trademark: | Karina |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DLN8GT_Karina-COMP-PVC-IVORY--E-75930-35-1-F-AC-HSF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HEAVY METAL FREE PVC COMPOUND - HIGH LEVEL OF OXYGEN - RECOMMENDED FOR EXTRUSION OF CABLE / WIRE COATING TYPES CM AND CMR. |
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.51 to 1.57 | g/cm³ | ASTM D792 |
| Cadmium Content | < 50 | ppm | ASTM D1971 |
| Chromium Content | < 100 | ppm | ASTM D1971 |
| Color | OK | ME 12 | |
| Color a | 0.850 to 2.85 | ME 12 | |
| Color b | 6.32 to 8.32 | ME 12 | |
| Color L | 85.6 to 87.6 | ME 12 | |
| Mercury Content | < 100 | ppm | ASTM D1971 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Lead Content | < 100 | ppm | ASTM D1971 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 15 sec) | 86 to 90 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | > 14.7 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | > 150 | % | ASTM D638 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | > 14.7 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | > 150 | % | ASTM D638 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 4 | > 1.0E+14 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | > 38 | % | ASTM D2863 |
| Note Message | |
|---|---|
| 1 . | 24 hr |
| 2 . | Aged in Air for 240 hr at 100°C |
| 3 . | Aged in Air for 240 hr at 100°C |
| 4 . | 24 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® A 30H1 V25 BLACK | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| Borealis PP RA130E-1498 | Borealis AG | PP Random Copolymer | Borealis PP |
| Elastron® V V100.A78.N | Elastron USA, Inc. | TPV | Elastron® V |
| MAJORIS DC407 - 7782 | AD majoris | PP, Unspecified | MAJORIS |
| POCAN® B 7375 000000 | LANXESS GmbH | PBT | POCAN® |