Strator® B-4
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | EPIC Polymers |
| Trademark: | Strator® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yXdXuS_Strator-B-4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| STRATOR® B-4 is a Polyamide 6 (Nylon 6) product filled with 40% long glass fiber. It is available in Europe. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.46 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.28 | -- | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.6 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ISO 527-2 | |||
| 23°C | 14500 | 9200 | MPa | |
| 90°C | 8500 | -- | MPa | |
| 120°C | 8200 | -- | MPa | |
| Tensile Stress | ISO 527-2 | |||
| Yield, 23°C | 215 | 150 | MPa | |
| Yield, 90°C | 120 | -- | MPa | |
| Yield, 120°C | 100 | -- | MPa | |
| Tensile Strain (Break, 23°C) | 2.4 | 2.7 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 12000 | 8200 | MPa | ISO 178 |
| Flexural Stress (23°C) | 300 | 190 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 28 | 35 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 90 | 100 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 220 | -- | °C | ISO 75-2/A |
| CLTE - Flow (23°C) | 2.3E-5 | -- | cm/cm/°C | ISO 7991 |
| Thermal Conductivity | 0.33 | -- | W/m/K | ISO 22007 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | -- | ohms | ASTM D257 |
| Electric Strength | 34 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 500 | -- | V | IEC 60112 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 240 to 280 | °C | |
| Middle Temperature | 250 to 290 | °C | |
| Front Temperature | 260 to 310 | °C | |
| Nozzle Temperature | 270 to 320 | °C | |
| Processing (Melt) Temp | < 320 | °C | |
| Mold Temperature | 80.0 to 130 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V969 NAT601 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Sindustris ABS LMA332 | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| TABOREN PH 42 T 40 | SILON s.ro | PP Homopolymer | TABOREN |
| Multi-Flex® TPO 2503 S | Multibase, A Dow Corning Company | TPO (POE) | Multi-Flex® TPO |
| VALOX™ 420SE0 resin | SABIC Innovative Plastics | PBT | VALOX™ |