SABIC® LDPE PCG09
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kNpA4C_SABIC-LDPE-PCG09.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® LDPE grades for healthcare applications are produced under controlled conditions resulting in high product quality, consistency and a high level of purity. SABIC® LDPE PCG09 is an additive free grade, typically designed for healthcare packaging and can typically be converted by Injection Molding and Cast Film to produce caps and closures, small bottles and secondary packaging. Compliance to Regulations SABIC® LDPE PCG09 complies with the relevant monographs of the European Pharmacopoeia (EP) and the United States Pharmacopoeia (USPVI). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.924 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 7.5 | g/10 min | |
| 190°C/5.0 kg | 25 | g/10 min | |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 190°C/2.16 kg | 10.0 | cm³/10min | |
| 190°C/5.0 kg | 33.0 | cm³/10min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Injection Molded) | 41 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 170 | MPa | ISO 527-2/1A/50 |
| Tensile Stress | ISO 527-2/1A/50 | ||
| Yield, Injection Molded | 9.00 | MPa | |
| Break, Injection Molded | 10.0 | MPa | |
| Tensile Strain (Break, Injection Molded) | 100 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C, Injection Molded | 8.0 | kJ/m² | |
| 23°C, Injection Molded | 50 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 46.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 93.0 | °C | ISO 306/A |
| Melting Temperature (DSC) | 110 | °C | DIN 53765 |
| Enthalpy Change | 138 | J/g | DIN 53765 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stirol UPS-0801 (extra) | JSC CONCERN STIROL | PS (HIPS) | Stirol |
| TOTAL Polystyrene Impact 825 | TOTAL Refining & Chemicals | PS (HIPS) | TOTAL Polystyrene |
| ALCOM® TCD PA66 5040 14016 | ALBIS PLASTIC GmbH | Nylon 66 | ALCOM® TCD PA66 |
| Aplax P2515GN | Ginar Technology Co., LTD. | PP, Unspecified | Aplax |
| Karina IVORY PVC COMP. -E 105908-35/ 1-C-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |