ULTEM™ AUR200G6 resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gbeza8_ULTEM-AUR200G6-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| The data listed in this data sheet are the lower specification limits, apart from the MFR, CTE, HDT at 1.8 MPa, Density, Tensile strain, Water Absorption, Thermal Conductivity and Shrinkage which are typical data. The MVR of this material at 337 degrees C/6.7 kgf will have a specification between 3 and 7.5 (MFR: 4.2-10.5) |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.53 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 7.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow 1 | 0.20 to 0.40 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.90 | % | |
| Equilibrium, 23°C, 50% RH | 0.50 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 120 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 6500 | MPa | ISO 178 |
| Flexural Stress | 180 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 3(23°C) | 4.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4 | |||
| 0.45 MPa, Unannealed, 100 mm Span | 205 | °C | ISO 75-2/Be |
| 1.8 MPa, Unannealed, 100 mm Span | 200 | °C | ISO 75-2/Ae |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 150°C | 2.5E-5 | cm/cm/°C | |
| Transverse : 23 to 150°C | 6.0E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.30 | W/m/K | ISO 8302 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 80.0 to 120 | °C | |
| Rear Temperature | 350 to 400 | °C | |
| Middle Temperature | 360 to 410 | °C | |
| Front Temperature | 370 to 420 | °C | |
| Nozzle Temperature | 360 to 410 | °C | |
| Processing (Melt) Temp | 370 to 410 | °C | |
| Mold Temperature | 140 to 180 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 |
| 4 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® LL4M 850 | Marco Polo International, Inc. | LLDPE | MARPOL® |
| VITAMIDE® AW38BK6150 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| Vydyne® 47H BK0668 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| Next ABS SX-02ABK | Next Polymers Ltd. | ABS | Next ABS |
| POLYfill PPC T5020 | Polykemi AB | PP Copolymer | POLYfill |