Jampilen RC1601
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | Jam Polypropylene Company |
| Trademark: | Jampilen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kG3cXT_Jampilen-RC1601.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Jampilen RC1601 is a unique clear polyolifinic resin specifically designed for skin layer of high barrier metalized BOPP film with high thermal resistance. It combines a high melting temperature with a high softening point; its superior thermal resistance prevents metal crazing during film converting in stressing conditions. Jampilen RC1601 is Calcium Stearate free and it does not contain migrating additives (slip agents, antistatics). Jampilen RC1601 is suitable for food contact. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1150 | MPa | ISO 527-2/1 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 75.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 140 | °C | ISO 306/A50 |
| Melting Temperature 1 | 150 | °C | ISO 11357-3 |
| Note Message | |
|---|---|
| 1 . | 20°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL AC-GP2 | Polymer Resources Ltd. | Acetal (POM) Copolymer | PRL |
| Tenac™ LA543 | Asahi Kasei Chemicals Corporation | Acetal (POM) Homopolymer | Tenac™ |
| Abistir® AR NATURALE | SO.F.TER. SPA | ABS | Abistir® |
| Boda FF3070 | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| Ferro PP TPP20AT08NA | Ferro Corporation | PP, Unspecified | Ferro PP |