Badatron® PPS CF40
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Bada AG |
| Trademark: | Badatron® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | k9BGHY_BadatronPPSCF40.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PPS-CF40, High strength and dimension stable 40% carbon fibres reinforced injection moulding grade |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.47 | g/cm³ | ISO 1183 |
| Water Absorption (Saturation, 23°C) | 0.030 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 33000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 185 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 0.60 | % | ISO 527-2/5 |
| Flexural Modulus 1(23°C) | 24000 | MPa | ISO 178 |
| Flexural Stress 2(23°C, 4.00 mm) | 235 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3(23°C) | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 4(23°C) | 25 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5(1.8 MPa, Unannealed, 4.00 mm) | 263 | °C | ISO 75-2/A |
| Melting Temperature (DSC) 6 | 295 | °C | ISO 3146 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 140 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 305 - 330 | °C | |
| Mold Temperature | 150 - 180 | °C |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 80x10x4 mm |
| 3 . | 80x10x4 mm |
| 4 . | 80x10x4 mm |
| 5 . | 110x10x4 mm |
| 6 . | Compound for molding, 10k/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 403 HI | RTP Company | PS (HIPS) | RTP |
| Prime ABS Film-X 100 | Primex Plastics Corporation | ABS | Prime ABS |
| UBE Polyethylene F320 | UBE America, Inc. | PE, Unspecified | UBE Polyethylene |
| Hanwha Total PE P200Y50 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | HDPE | Hanwha Total PE |
| Hylon® N2213STHL | Ravago Manufacturing Americas, LLC | Nylon 6 | Hylon® |