Eltex® PF1320AZ

Category:	mLLDPE , Metallocene Linear Low Density Polyethylene
Manufacturer:	INEOS Olefins & Polymers Europe
Trademark:	Eltex®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	k2fvYa_EltexPF1320AZ.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Additive free C6 m-LLDPE for extrusion coating, injection moulding and compounding.

Benefits & Features

outstanding ESCR performance

improved sealing performance

improved mechanical properties

Applications
For extrusion coating:

extrusion coating polymer for high demand on sealing and mechanical performance

For injection moulding and compounding:

absence of any kind of additive allowing tailor formulation of specific compounds and master-batches

General Information
Features	Low density High ESCR (Stress Cracking Resistance) No additive
Uses	Composite Masterbatch Coating application
RoHS Compliance	Contact manufacturer
Forms	Particle
Processing Method	Composite Extrusion coating Injection molding

Physical	Nominal Value	Unit	Test Method
Density (23°C)	0.913	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	20	g/10 min	ISO 1133
Environmental Stress-Cracking Resistance (Compression Molded)	29.0	hr	Internal method

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D, Compression Molded)	46		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (Compression Molded)	225	MPa	ISO 527-2
Tensile Stress (Yield, 23°C, Compression Molded)	8.00	MPa	ISO 527-2
Tensile Strain			ISO 527-2
Yield, molding	18	%	ISO 527-2
Fracture, molding	> 600	%	ISO 527-2
Flexural Modulus (23°C, Compression Molded)	260	MPa	ISO 178
Tensile fracture strength- Compression Molded	No Break		ISO 527-2

Thermal	Nominal Value	Unit	Test Method
Heat of Fusion	101	J/g	ASTM D3418

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (-20°C, Compression Molded)	70	kJ/m²	ISO 180/A

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	88.0	°C	ISO 306/A50
Melting Temperature ¹	96.0 - 114	°C	ISO 11357-3
Peak Crystallization Temperature	82 - 101	°C	Internal method

Injection	Nominal Value	Unit
Processing (Melt) Temp	< 280	°C

Extrusion	Nominal Value	Unit
Melt Temperature	< 280	°C

Note Message
1 .	DSC 2nd heating 10°C/min

Resin Grade	Manufacturer	Category	Trademark
Tecnoprene® T60 VB4 NERO900	SO.F.TER. SPA	PP, Unspecified	Tecnoprene®
TAIRIPRO K7005AX	Formosa Plastics Corporation	PP Impact Copolymer	TAIRIPRO
HiFill® PS GB40	Techmer Engineered Solutions	PS (GPPS)	HiFill®
HIPOL™ J740	Mitsui Chemicals, Inc.	PP Impact Copolymer	HIPOL™
MAJORIS AT367	AD majoris	PP Copolymer	MAJORIS