Spartech Polycom SC14-1213
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Spartech Polycom |
| Trademark: | Spartech |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | isipxv_Spartech-Polycom-SC14-1213.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Available with or without lube and/or heat stabilizer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.70 - 1.1 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4480 | MPa | ASTM D638 |
| Tensile Strength (Break) | 103 | MPa | ASTM D638 |
| Flexural Modulus | 4480 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 159 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 245 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 1.0 - 4.0 | hr | |
| Rear Temperature | 288 - 299 | °C | |
| Middle Temperature | 277 - 282 | °C | |
| Front Temperature | 271 - 277 | °C | |
| Nozzle Temperature | 282 - 293 | °C | |
| Processing (Melt) Temp | 288 - 310 | °C | |
| Mold Temperature | 65.6 - 121 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCLAIR® 19C | NOVA Chemicals | HDPE | SCLAIR® |
| NOVAPOL® PF-Y821 Series | NOVA Chemicals | LLDPE | NOVAPOL® |
| ALTECH® PA66 A 2030/589 GF30 | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |
| HAIPLEN EP50 C2 | Taro Plast S.p.A. | PP Copolymer | HAIPLEN |
| Moplen HP420J | PolyMirae | PP Homopolymer | Moplen |