TOTAL Polystyrene Compound 881
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polystyrene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iEK2W9_TOTALPolystyreneCompound881.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TOTAL POLYSTYRENE 881 is a high flow, V0 brominated flame retardant, high impact polystyrene for injection molding application. This grade is recommended for manufacturing of articles which require good dimensional stability. Applications
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 15 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 - 0.70 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | < 0.10 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 93 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 20.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 40 | % | ISO 527-2 |
| Flexural Modulus | 1700 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 7.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 90.0 | °C | ISO 306/A50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+13 | ohms | IEC 60093 |
| Dielectric Strength | 150 | kV/mm |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.4 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | < 240 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zhongfa PA66 ST-12 | Yuyao Zhongfa Engineering Plastics Co. Ltd. | Nylon 66 | Zhongfa |
| ALFATER XL® A70I 2GP0050 | ALBIS PLASTIC GmbH | TPV | ALFATER XL® |
| Geon™ Vinyl Wire & Cable WJJK501 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Wire & Cable |
| Infino NH-3402F | SAMSUNG SDI CO., LTD. | PC | Infino |
| P-FLEX R 2620 | Putsch Kunststoffe GmbH | ABS | P-FLEX |