LEXAN™ 123X resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | i8wsYI_LEXAN-123X-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Improved flow PC with excellent processability and mold release. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 20 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (220°C/5.0 kg) | 18.6 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 0.80 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.35 | % | |
| Equilibrium, 23°C, 50% RH | 0.15 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2320 | MPa | ASTM D638 |
| -- | 2450 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 60.0 | MPa | ASTM D638 |
| Yield | 60.0 | MPa | ISO 527-2/50 |
| Break 3 | 60.0 | MPa | ASTM D638 |
| Break | 59.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 6.0 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/50 |
| Break 5 | 120 | % | ASTM D638 |
| Break | 120 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2360 | MPa | ASTM D790 |
| -- 7 | 2310 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 71.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 96.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9 | ISO 179/1eA | ||
| -30°C | 12 | kJ/m² | |
| 23°C | 65 | kJ/m² | |
| Charpy Unnotched Impact Strength 10 | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact | |||
| -30°C | 240 | J/m | ASTM D256 |
| 23°C | 830 | J/m | ASTM D256 |
| -30°C 11 | 11 | kJ/m² | ISO 180/1A |
| 23°C 12 | 65 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 13 | ISO 180/1U | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Instrumented Dart Impact (23°C, Total Energy) | 72.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 128 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 6.40 mm | 129 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 14 | 122 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 141 | °C | ASTM D1525, ISO 306/B50 11 15 |
| -- | 143 | °C | ISO 306/B120 |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 6.0E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 6.0E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 271 to 293 | °C | |
| Middle Temperature | 282 to 304 | °C | |
| Front Temperature | 293 to 316 | °C | |
| Nozzle Temperature | 288 to 310 | °C | |
| Processing (Melt) Temp | 293 to 316 | °C | |
| Mold Temperature | 71.1 to 93.3 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*3 sp=62mm |
| 10 . | 80*10*3 sp=62mm |
| 11 . | 80*10*3 |
| 12 . | 80*10*3 |
| 13 . | 80*10*3 |
| 14 . | 80*10*4 mm |
| 15 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Melthene® -M M5002D | TOSOH Corporation | Polyolefin, Unspecified | Melthene® -M |
| VESTAMID® D DX9325 | Evonik Industries AG | Nylon 612 | VESTAMID® D |
| TPUCO® TPUE-E80 | Taiwan PU Corporation | TPU-Polyester | TPUCO® |
| Elastollan® 1190A16 | BASF Corp. Thermoplastic Polyurethanes | TPU-Polyether | Elastollan® |
| KEBAFLEX® S 45 A.01 | BARLOG plastics GmbH | TES | KEBAFLEX® |