Catalyst PS/2 LR0 Black Datasheet,Polyolefin, Unspecified,Solvay Specialty Polymers-SHANGHAI SUSHENG

Message
Catalyst PS/2 LR0 Black is a PE based black catalyst masterbatch. The black catalyst PS/2 LR0 Black contains a processing aid.

General Information
Features	Antioxidation Good UV resistance Good thermal aging resistance
Uses	Pipe components Piping system Potable water application
Processing Method	Pipeline extrusion molding Extrusion

Physical	Nominal Value	Unit	Test Method
Density	1.10	g/cm³	ASTM D792
Apparent Density	0.65	g/cm³	ISO 60

Additional Information
Above values are typical averagesUse and DosageCatalyst PS/2 LR0 Black shall be used together with the silane-crosslinkable POLIDAN® compounds in the ratio of 7 to 93 parts respectively. The two components shall be mixed together before the extrusion or continuously during the process with the use of automatic feeders.Catalyst PS/2 LR0 Black can be dried before use at 80°C for 4h.StorageThe product shall be stored under the following conditions: Closed and unbroken bags Ambient temperature not exceeding 40°C Indoor in order to avoid direct exposure to sunlight The product could undergo alterations due to extended period of storage. Solvay Specialty Polymers suggests the product use within 12 months from the production date printed on the packaging. Solvay Specialty Polymers accepts no liability of any kind in case the above mentioned conditions are not fulfilled.PackagingCatalyst PS/2 LR0 Black is supplied in 25 kg bags placed on pallets.Technical ServiceCatalyst PS/2 LR0 Black is part of the Solvay Specialty Polymers catalyst masterbatch range and is used together with the POLIDAN® compounds. Solvay Specialty Polymers Technical Service is available to assist customers with further information and advice including the start-up and also for any eventual necessity during the use of the product.

Additional Information

Above values are typical averagesUse and DosageCatalyst PS/2 LR0 Black shall be used together with the silane-crosslinkable POLIDAN® compounds in the ratio of 7 to 93 parts respectively. The two components shall be mixed together before the extrusion or continuously during the process with the use of automatic feeders.Catalyst PS/2 LR0 Black can be dried before use at 80°C for 4h.StorageThe product shall be stored under the following conditions: Closed and unbroken bags Ambient temperature not exceeding 40°C Indoor in order to avoid direct exposure to sunlight The product could undergo alterations due to extended period of storage. Solvay Specialty Polymers suggests the product use within 12 months from the production date printed on the packaging. Solvay Specialty Polymers accepts no liability of any kind in case the above mentioned conditions are not fulfilled.PackagingCatalyst PS/2 LR0 Black is supplied in 25 kg bags placed on pallets.Technical ServiceCatalyst PS/2 LR0 Black is part of the Solvay Specialty Polymers catalyst masterbatch range and is used together with the POLIDAN® compounds. Solvay Specialty Polymers Technical Service is available to assist customers with further information and advice including the start-up and also for any eventual necessity during the use of the product.

Extrusion	Nominal Value	Unit
Cylinder Zone 1 Temp.	150 - 200	°C
Cylinder Zone 2 Temp.	150 - 200	°C
Cylinder Zone 3 Temp.	150 - 200	°C
Cylinder Zone 4 Temp.	150 - 200	°C
Cylinder Zone 5 Temp.	150 - 200	°C
Head Temperature	200	°C
Extruder Screw L/D Ratio	25:1 to 30:1
Extruder Screw Compression Ratio	>2.5:1
Die Temperature	210	°C

Extrusion instructions
Typical extrusion temperatures in combination to POLIDAN® crosslinkable grades

Category:	Polyolefin, Unspecified , Polyolefin
Manufacturer:	Solvay Specialty Polymers
Trademark:	Catalyst
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	htfN7P_CatalystPS2LR0Black.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
REPOL® H026SG	Reliance Industries Limited	PP Homopolymer	REPOL®
VALOX™ 420HP resin	SABIC Innovative Plastics	PBT	VALOX™
Zytel® HTN 52G35EF BK420	DuPont Performance Polymers	PPA	Zytel® HTN
LNP™ LUBRICOMP™ DBL32 compound	SABIC Innovative Plastics	PC	LNP™ LUBRICOMP™
LNP™ LUBRICOMP™ WFL36 compound	SABIC Innovative Plastics	PBT	LNP™ LUBRICOMP™