Adell PBT HR-16
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Adell Plastics, Inc. |
| Trademark: | Adell PBT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | htBmrE_Adell-PBT-HR-16.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Adell PBT HR-16 is a Polybutylene Terephthalate (PBT) material filled with 30% glass fiber. It is available in North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.53 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.20 to 0.50 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.60 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 78 | ||
| R-Scale | 118 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 148 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus | 8550 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 203 | MPa | ASTM D790 |
| Compressive Strength | 124 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 96 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 216 | °C | |
| 1.8 MPa, Unannealed | 210 | °C | |
| Melting Temperature | 238 to 249 | °C | |
| CLTE - Flow | 2.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 3.2E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 19 | kV/mm | ASTM D149 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SIMONA® PVC VS-1 | SIMONA AMERICA, Inc. | PVC, Rigid | SIMONA® |
| TUFNYL® SGF 15 RED | SRF Ltd. | Nylon 6 | TUFNYL® |
| AT 520 | Celanese EVA Performance Polymers | LDPE | AT |
| Globalene® 6231-20 | Lee Chang Yung Chemical Industry Corp. | PP Homopolymer | Globalene® |
| 3M™ Dyneon™ PTFE Compound TF R4212 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |