MonoSol® AF L330
| Category: | PVOH , Polyvinyl Alcohol |
| Manufacturer: | MonoSol, LLC |
| Trademark: | MonoSol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sedhai_MonoSol-AF-L330.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MonoSol AF L300 is a PVOH based thermoplastic film, soluble in cold water and manufactured using MonoSol's proprietary solution cast technology. MonoSol AF L330 is a typical grade of PVOH cold water-soluble packaging film and is the film choice for powders with no special requirements or contraindications. This tough film has good solubility, machinability, toughness and cold crack resistance. It is available in bags and can be converted on most vertical form fill and rotorary forming packaging machines. Available thickness range is 20 micron (0.8 mil) to 80 micron (3.1 mil). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Moisture Content (23°C) 1 | 6.7 | wt% | |
| Solubility 2 | |||
| Disintegration : 10°C, 60.0 µm | 31.0 | sec | |
| Dissolution : 10°C, 60.0 µm | 95.0 | sec |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Yield (60.0 µm) | 13.4 | m²/kg | ASTM D4321 |
| Film Thickness - Tested | 60 | µm | |
| Film Thickness - Recommended / Available | 20 µm to 80 µm | ||
| Secant Modulus | ASTM D882, ISO 527-3 | ||
| 10%, MD : 60 µm | 77.9 | MPa | |
| 100%, MD : 60 µm | 26.9 | MPa | |
| 10%, TD : 60 µm | 66.2 | MPa | |
| 100%, TD : 60 µm | 14.5 | MPa | |
| Tensile Strength | |||
| MD : Break, 60 µm | 43.4 | MPa | ASTM D882 |
| TD : Break, 60 µm | 32.4 | MPa | ASTM D882 |
| MD : 60 µm | 43.4 | MPa | ISO 527-3 |
| TD : 60 µm | 32.4 | MPa | ISO 527-3 |
| Tensile Elongation | ASTM D882, ISO 527-3 | ||
| MD : Break, 60 µm | 220 | % | |
| TD : Break, 60 µm | 380 | % | |
| Elmendorf Tear Strength | |||
| MD : 60 µm | 1300 | g | ASTM D1922 |
| TD : 60 µm | 1300 | g | ASTM D1922 |
| MD : 60 µm | 0.13 | N | ISO 6383-2 |
| TD : 60 µm | 0.13 | N | ISO 6383-2 |
| Note Message | |
|---|---|
| 1 . | 50%RH |
| 2 . | Distilled Water (MSTM 205) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shinite® PBT D202 | Shinkong Synthetic Fiber Corp. | PBT | Shinite® PBT |
| Tecnoprene® AKM43F NAT005 | SO.F.TER. SPA | PP Homopolymer | Tecnoprene® |
| Ferro PP TPP40AD37NA | Ferro Corporation | PP Homopolymer | Ferro PP |
| Iupilon® GSH2020SR 9920A | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| POCAN® BFN 4231 000000 | LANXESS GmbH | PBT | POCAN® |