SMOKEGUARD™ III 1028 NATURAL
| Category: | PVC, Unspecified , Polyvinyl Chloride |
| Manufacturer: | AlphaGary |
| Trademark: | SMOKEGUARD™ III |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hofkB6_SMOKEGUARD-III-1028-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SMOKEGUARD III 1028 IS A LEAD FREE, 75°C DEGREE, HIGHLY FLAME RETARDED, LOW SMOKE JACKETING COMPOUND FOR PLENUM CABLE CONSTRUCTIONS. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.56 - 1.60 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw D | 65 - 71 | ASTM D2240 | |
| Shaw D, 15 seconds | 50 - 56 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D412 | ||
| 0.381 mm | 17.2 | MPa | ASTM D412 |
| 1.91 mm | 15.2 | MPa | ASTM D412 |
| Tensile Elongation | ASTM D412 | ||
| Fracture, 1.91mm | 210 | % | ASTM D412 |
| Fracture, 0.381mm | 190 | % | ASTM D412 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -8.00 | °C | ASTM D746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Constant (23°C, 100 MHz) | 3.30 | ASTM D150 | |
| Dissipation Factor (23°C, 100 MHz) | 0.014 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index (3.18 mm) | 47 | % | ASTM D2863 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 149 | °C | |
| Cylinder Zone 2 Temp. | 154 | °C | |
| Cylinder Zone 3 Temp. | 163 | °C | |
| Cylinder Zone 4 Temp. | 168 | °C | |
| Cylinder Zone 5 Temp. | 168 | °C | |
| Adapter Temperature | 154 | °C | |
| Melt Temperature | 179 - 185 | °C | |
| Die Temperature | 154 | °C | |
| Extruder Screw Compression Ratio | 3.0:1.0 |
| Extrusion instructions |
|---|
| Melt temperature is critical, at temperatures above 370 degrees F foaming may occur. It may be necessary to adjust barrel temp to attain the desired melt temp. Material should be dried prior to use |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Network Polymers LLDPE 11 5026 | Network Polymers, Inc. | LLDPE | Network Polymers LLDPE |
| CP PRYME® Polypropylene PPC100-20M | Chase Plastics Services Inc. | PP Copolymer | CP PRYME® Polypropylene |
| Elastron® G G400.D40.N | Elastron USA, Inc. | SEBS | Elastron® G |
| InvisiSil™ IVS4542 | Momentive Performance Materials Inc. | Silicone | InvisiSil™ |
| LNP™ THERMOCOMP™ DX13354X compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ THERMOCOMP™ |