Order Products : sales@su-jiao.com
Ateva® 1221
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Celanese EVA Performance Polymers |
| Trademark: | Ateva® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RcQMGx_Ateva-1221.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| This resin is commonly used for coextrusion and blending applications where superior strength, good heat seal, and hot tack characteristics are required. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.932 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.80 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 12.0 | wt% |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus - 1% Secant | 84.0 | MPa | ASTM D790 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D882A | ||
| MD : Break | 27.0 | MPa | |
| TD : Break | 28.0 | MPa | |
| Tensile Elongation 2 | ASTM D882A | ||
| MD : Break | 400 | % | |
| TD : Break | 510 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 78.0 | °C | ASTM D1525 |
| Peak Melting Temperature | 97.0 | °C | ASTM D3418 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | < 210 | °C |
| Note Message | |
|---|---|
| 1 . | 500 mm/min |
| 2 . | 500 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MIDILENA III HDPE RBF0.08 | ROMPETROL PETROCHEMICALS S.R.L. | HDPE | MIDILENA III |
| Nycal™ 1850R33 | Technical Polymers, LLC | Nylon 6 | Nycal™ |
| Evermore PUR UP-9341NHR | Evermore Chemical Industry Co., Ltd. | PUR-Ether | Evermore PUR |
| TECHNYL® C 246 NATURAL | Solvay Engineering Plastics | Nylon 6 | TECHNYL® |
| LG ABS AF365F | LG Chem Ltd. | ABS | LG ABS |