AKROMID® A4 1 natural (3716)
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hm89mL_AKROMID-A4-1-natural-3716-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® A4 1 natural (3716) is a nonreinforced, heat stabilised, higher viscous polyamide 6.6 with light inherent color Applications are highly stressed parts such as gear-wheels, bearing cages, cable connectors and coil formers. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.14 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 20.0 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.8 | -- | % | |
| Flow | 1.5 | -- | % | |
| Humidity Absorption - 62% RH (70°C) | 2.4 to 2.8 | -- | % | ISO 1110 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flexural Strain at Break 1 | 7.0 | -- | % | ISO 178 |
| Tensile Modulus | 3000 | 1400 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 90.0 | 55.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | |||
| Yield | 4.5 | 20 | % | |
| Break | > 30 | > 50 | % | |
| Flexural Modulus 2 | 3000 | -- | MPa | ISO 178 |
| Flexural Stress 3 | 125 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 3.5 | -- | kJ/m² | |
| 23°C | 7.0 | 15 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ||
| 23°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 1.8 MPa, Unannealed | 72.0 | -- | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 52.0 | -- | °C | ISO 75-2/C |
| Melting Temperature 4 | 260 | -- | °C | DIN EN 11357-1 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 5(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 10 K/min, DSC |
| 5 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8331-72FUV Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| MTEGRITY™ HDPE HD360 | M. Holland Company | HDPE | MTEGRITY™ HDPE |
| VITAMIDE® BR12 | A. Schulman Europe | Nylon 6 | VITAMIDE® |
| BJB Polyurethane TC-690 A/B | BJB Enterprises, Inc. | TSU | BJB Polyurethane |
| MAJORIS DE289 | AD majoris | PP, Unspecified | MAJORIS |