LNP™ STAT-KON™ DD0001 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hiORyP_LNP-STAT-KON-DD0001-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON* DD0001 is a compound based on Polycarbonate resin containing Carbon Powder. Added features of this material include: Electrically Conductive, Flame Retardant. Also known as: LNP* STAT-KON* Compound D-FR ECO Product reorder name: DD0001 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.40 | % | ASTM D955 |
| Across Flow : 24 hr | 0.40 | % | ASTM D955, ISO 294-4 |
| Flow : 24 hr | 0.39 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.11 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.14 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3450 | MPa | ASTM D638 |
| -- | 3750 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 64.3 | MPa | ASTM D638 |
| Break | 64.6 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 3.7 | % | ASTM D638 |
| Break | 3.2 | % | ISO 527-2 |
| Flexural Modulus | 3520 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | |||
| -- | 117 | MPa | ASTM D790 |
| -- | 103 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 23 | J/m | ASTM D256 |
| 23°C 2 | 2.4 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 550 | J/m | ASTM D4812 |
| 23°C 3 | 37 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 1.93 | J | ASTM D3763 |
| -- | 0.700 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 86.7 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 88.4 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 82.2 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 82.0 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 5.2E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 5.2E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+6 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.70 mm, Testing by SABIC) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 249 to 260 | °C | |
| Middle Temperature | 254 to 266 | °C | |
| Front Temperature | 260 to 271 | °C | |
| Processing (Melt) Temp | 254 to 288 | °C | |
| Mold Temperature | 37.8 to 65.6 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Niuk YPC8003 | Shanghai Niuk New Plastic Technology Co., Ltd. | Acetal (POM) Copolymer | Niuk |
| Geon™ Vinyl Rigid Molding M3815 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Molding |
| Ketjenflex® MS 80 | Axcentive SARL | Plasticizer | Ketjenflex® |
| Latigray 52/11-01 CX/70 | LATI S.p.A. | PP Homopolymer | Latigray |
| Clyrell RC549S | LyondellBasell Industries | PP Random Copolymer | Clyrell |