Arnitel® PL460-S
| Category: | TPC-ET , Thermoplastic Copolyester Elastomer |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Arnitel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xBIouM_Arnitel-PL460-S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Arnitel® PL460-S is a Thermoplastic Copolyester Elastomer (TPC-ET) material. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of Arnitel® PL460-S are:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (240°C/2.16 kg) | 18.0 | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 3.5 | % | |
| Equilibrium, 23°C, 50% RH | 0.40 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 60 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 240 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Break | 21.3 | MPa | |
| 10% Strain | 10.6 | MPa | |
| 100% Strain | 16.1 | MPa | |
| Nominal Tensile Strain at Break | 240 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 22 | kJ/m² | |
| 23°C | 60 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature 1 | 220 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 5.30 | ||
| 1 MHz | 4.80 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flammability Classification (1.50 mm) | V-0 | IEC 60695-11-10, -20 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 200 to 220 | °C | |
| Middle Temperature | 210 to 230 | °C | |
| Front Temperature | 220 to 240 | °C | |
| Nozzle Temperature | 230 to 250 | °C | |
| Processing (Melt) Temp | 230 to 250 | °C | |
| Mold Temperature | 20.0 to 50.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 287E | RTP Company | Nylon, Unspecified | RTP |
| RTP 205 | RTP Company | Nylon 66 | RTP |
| RTP PP FR2 NAT | RTP Company | PP, Unspecified | RTP |
| StarTUFF TF 55-HR-9 | STAR Thermoplastic Alloys & Rubbers, Inc. | TPE | StarTUFF |
| TAROPRENE® 1 A75 M1N | Taro Plast S.p.A. | TPV | TAROPRENE® |