COPYLENE® CR020CL
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | Phillips 66 |
| Trademark: | COPYLENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hGGKqH_COPYLENE-CR020CL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
COPYLENE ® CR020CL is a random copolymer formulated with advanced clarifier technology and with antistat and is specially designed to excel in extrusion blowmolding processes. EBM bottles will have exceptional gloss and low haze. Applications:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.902 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 28.2 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 14 | % | ASTM D638 |
| Flexural Modulus - 1% Secant 2 | 1100 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 340 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 80.0 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 1.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nypol® PA B3 G10 T10 NTLA010 NT383 | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| ALCOM® PC + ABS 750/8 PTFE8 | ALBIS PLASTIC GmbH | PC+ABS | ALCOM® PC + ABS |
| alphalon™ 33 | Grupa Azoty ATT Polymers GmbH | Nylon 6 | alphalon™ |
| HiFill® PA6 IM 409 L MB | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| TECHNYL® C 216 V50 BLACK Z | Solvay Engineering Plastics | Nylon 6 | TECHNYL® |