| Polypropylene copolymer medium flow, flame rating UL94 HB. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Vertical flow direction : 23°C, 3.20mm | 1.4 - 1.8 | % | Internal method |
| Flow direction : 23°C, 3.20mm | 1.4 - 1.8 | % | Internal method |
| Water Absorption (Saturation, 23°C) | 0.020 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 22.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 80 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 1100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 100 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 115 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 55.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 75.0 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 190 - 220 | °C | |
| Mold Temperature | 40.0 - 60.0 | °C | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Pre-heat Temperature: 70 to 80°CPre-heat Time: 1 hr |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Dugdale PVC Flexible Extrusion - Shore A 74 Compound | Dugdale Plc | PVC, Flexible | Dugdale PVC |
| FastFlex Brushable | BJB Enterprises, Inc. | TSU | FastFlex |
| Dynaflex™ G2709-1000-00 | PolyOne Corporation | TPE | Dynaflex™ |
| Lucent PC PC/PBT-1020 | Lucent Polymers, Inc. | PC+PBT | Lucent PC |
| Hostacom EKC 265N 2 G82732 | LyondellBasell Industries | PP Copolymer | Hostacom |