Durethan® BKV 50 H2.0 901510
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 070kNv_DurethanBKV50H20901510.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 50 % glass fibers, injection molding, heat-aging stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | ||||
| -- | 1.57 | -- | g/cm³ | ASTM D792 |
| 23°C | 1.57 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | -- | g/cm³ | ISO 60 |
| Molding Shrinkage | ISO 2577 | |||
| Vertical flow direction : 280°C, 3.00mm 1 | 0.85 | -- | % | ISO 2577 |
| Vertical flow direction : 120°C, 4 hours, 3.00mm 2 | 0.050 | -- | % | ISO 2577 |
| Flow direction : 280°C, 3.00mm 3 | 0.16 | -- | % | ISO 2577 |
| Flow direction : 120°C, 4 hours, 3.00mm 4 | 0.020 | -- | % | ISO 2577 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 5.0 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.5 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 250 | 109 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ||||
| 23°C 5 | 15000 | 9500 | MPa | ASTM D638 |
| 23°C | 16300 | 9800 | MPa | ISO 527-2/1 |
| Tensile Strength | ||||
| Fracture, 23°C | 210 | 150 | MPa | ASTM D638 |
| Fracture, 23°C | 220 | 140 | MPa | ISO 527-2/5 |
| Tensile Elongation | ||||
| Fracture, 23°C | 2.0 | 4.0 | % | ASTM D638 |
| Fracture, 23°C | 3.0 | 5.0 | % | ISO 527-2/5 |
| Tensile Creep Modulus | ISO 899-1 | |||
| 1 hr | -- | 8100 | MPa | ISO 899-1 |
| 1000 hr | -- | 6600 | MPa | ISO 899-1 |
| Flexural Modulus | ||||
| 23°C | 13500 | 7690 | MPa | ASTM D790 |
| 23°C 6 | 15100 | 9700 | MPa | ISO 178/A |
| Flexural Strength | ||||
| 23°C | 350 | 220 | MPa | ASTM D790 |
| 23°C 7 | 360 | 230 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 8(23°C) | 3.0 | 5.0 | % | ISO 178/A |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Behavior 9(> 1.00 mm) | passed | -- | ISO 3795 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6, GHR, 14-160, GF50 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 - 0.12 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 15 | 13 | kJ/m² | ISO 179/1eA |
| 23°C | 20 | 25 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 85 | 80 | kJ/m² | ISO 179/1eU |
| 23°C | 100 | 100 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ||||
| -40°C, 3.18 mm | 130 | 130 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 170 | 200 | J/m | ASTM D256 |
| -30°C | 12 | 12 | kJ/m² | ISO 180/1A |
| 23°C | 20 | 25 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 80 | 80 | kJ/m² | ISO 180/1U |
| 23°C | 85 | 85 | kJ/m² | ISO 180/1U |
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | |||
| -30°C | 3.70 | -- | J | ISO 6603-2 |
| 23°C | 4.20 | 8.90 | J | ISO 6603-2 |
| Multi-Axial Instrumented Impact Peak Force | ISO 6603-2 | |||
| -30°C | 1060 | -- | N | ISO 6603-2 |
| 23°C | 1200 | -- | N | ISO 6603-2 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, unannealed, 39.9mm | 215 | -- | °C | ASTM D648 |
| 0.45 MPa, not annealed | 215 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 205 | -- | °C | ISO 75-2/A |
| 1.8 MPa, annealing, 3.99mm | 200 | -- | °C | ASTM D648 |
| Vicat Softening Temperature | > 200 | -- | °C | ISO 306/B50, ISO 306/B120 |
| Melting Temperature 10 | 222 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 55°C | 2.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 7.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| RTI Elec | UL 746 | |||
| 0.750 mm | 65.0 | -- | °C | UL 746 |
| 1.50 mm | 120 | -- | °C | UL 746 |
| RTI Imp | UL 746 | |||
| 0.750 mm | 65.0 | -- | °C | UL 746 |
| 1.50 mm | 95.0 | -- | °C | UL 746 |
| RTI | UL 746 | |||
| 0.750 mm | 65.0 | -- | °C | UL 746 |
| 1.50 mm | 140 | -- | °C | UL 746 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 - 1.0E+14 | 1.0E+12 - 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+15 - 1.0E+16 | 1.0E+12 - 1.0E+13 | ohms·cm | IEC 60093 |
| Dielectric Strength | IEC 60243-1 | |||
| 23°C, 1.00 mm | 35 | 26 | kV/mm | IEC 60243-1 |
| 23°C, 3.00 mm | 40 | 35 | kV/mm | IEC 60243-1 |
| Dielectric Constant | IEC 60250 | |||
| 23°C, 50 Hz 11 | 4.00 | -- | IEC 60250 | |
| 23°C, 1 MHz 12 | 4.00 | 5.00 | IEC 60250 | |
| 23°C, 100 Hz | 5.30 | 14.2 | IEC 60250 | |
| 23°C, 1 MHz | 4.30 | 5.00 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | |||
| 23°C, 50 Hz | 0.010 | -- | IEC 60250 | |
| 23°C, 100 Hz | 0.036 | 0.32 | IEC 60250 | |
| 23°C, 1 MHz | 0.015 0.024 | 0.14 0.089 | IEC 60250 | |
| Comparative Tracking Index | ||||
| Solution a | 550 | -- | V | IEC 60112 |
| -- | -- | 375 | V | ASTM D3638 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.750 mm | HB | -- | UL 94 | |
| 1.50 mm | HB | -- | UL 94 | |
| 1.60 mm | HB | -- | UL 94 | |
| 3.00 mm | HB | -- | UL 94 | |
| 3.20 mm | HB | -- | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Oxygen Index 13 | 24 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 270 - 290 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Note Message | |
|---|---|
| 1 . | 150x105x3mm, 80°C MT, 400 bar |
| 2 . | 150x105x3mm |
| 3 . | 150x105x3mm, 80°C MT, 400 bar |
| 4 . | 150x105x3mm |
| 5 . | 1.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 2 mm/min |
| 9 . | US-FMVSS302 |
| 10 . | 10°C/min |
| 11 . | Tinfoil Electrodes |
| 12 . | Tinfoil Electrodes |
| 13 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen RP348N | LyondellBasell Industries | PP Random Copolymer | Moplen |
| BCC Resins MB2001 | BCC Products Inc. | PUR, Unspecified | BCC Resins |
| Fainplast PVC PK 8350 | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| ICORENE® N2101 | ICO Polymers EMEA, A Division of A. Schulman | LDPE | ICORENE® |
| SEQUEL® 1492-UV NH647 MET GD | LyondellBasell Industries | PP, Unspecified | SEQUEL® |