Thermx® CG023
| Category: | PCT , Polycyclohexylenedimethylene Terephthalate |
| Manufacturer: | Celanese Corporation |
| Trademark: | Thermx® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gw6xe4_Thermx-CG023.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Thermx® CG023 is a 20% glass fiber reinforced polycyclohexylenedimethylene terephthalate for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.38 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/2.16 kg) | 30.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.80 | % | |
| Flow | 0.30 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6400 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 100 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.3 | % | ISO 527-2/1A/5 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 6000 | MPa | |
| 1000 hr | 4600 | MPa | |
| Flexural Modulus (23°C) | 5800 | MPa | ISO 178 |
| Flexural Stress (23°C) | 155 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 7.0 | kJ/m² | |
| 23°C | 7.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 30 | kJ/m² | |
| 23°C | 35 | kJ/m² | |
| Notched Izod Impact Strength (23°C) | 6.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 253 | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 105 | °C | ISO 11357-2 |
| Melting Temperature 2 | 285 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 3.0E-5 | cm/cm/°C | |
| Transverse | 8.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 41 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density of Melt | 1.140 | g/cm³ | Internal Method |
| Ejection Temperature | 230 | °C | Internal Method |
| Specific Heat Capacity of Melt | 1470 | J/kg/°C | Internal Method |
| Thermal Conductivity of Melt | 0.20 | W/m/K | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 95.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Processing (Melt) Temp | 295 to 310 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 2933-70 White 1503 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| DOW™ LDPE 330E | The Dow Chemical Company | LDPE | DOW™ LDPE |
| ADEKA EP-4010S | Adeka Corporation | Epoxy | ADEKA |
| ICORENE® K 4140 | ICO Polymers SA, A Division of A. Schulman | XLPE | ICORENE® |
| Sumiliteresin® PR-53800 | SBHPP | Phenolic | Sumiliteresin® |