LNP™ THERMOCOMP™ MFB22EXJ compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HTBurL_LNPTHERMOCOMPMFB22EXJcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* THERMOCOMP* MFB22EXJ is a compound based on Polypropylene resin containing Glass Fiber, Glass Bead. Added features of this grade are: Easy Molding, High Flow, Healthcare. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (210°C/5.0 kg) | 12 - 20 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 4090 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 34.0 | MPa | ASTM D638 |
| Fracture | 30.0 | MPa | ASTM D638 |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 3.9 | % | ASTM D638 |
| Fracture | 6.7 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 2970 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 50.0 mm Span) | 50.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 40 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 100 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Scolefin 33 G 10-0 | Ravago Group | PP Homopolymer | Scolefin |
| Niuk 23RN60 | Shanghai Niuk New Plastic Technology Co., Ltd. | PC+ABS | Niuk |
| PLUSTEK PB891 | Polyram Ram-On Industries | Nylon 6 | PLUSTEK |
| LNP™ LUBRICOMP™ EX06405 compound | SABIC Innovative Plastics | PEI | LNP™ LUBRICOMP™ |
| XENOY™ 5720U resin | SABIC Innovative Plastics | PC+PBT | XENOY™ |