Fortron® MT9115L0 DW
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Celanese Corporation |
| Trademark: | Fortron® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gphFAQ_Fortron-MT9115L0-DW.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Fortron® MT9115L0 DW is a 15% fiberglass-reinforced grade of polyphenylene sulfide with high melt strength suitable for blow molding and extrusion applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.44 | g/cm³ | ISO 1183 |
| Water Absorption (Saturation, 23°C) | 0.020 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7700 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 120 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 7500 | MPa | ISO 178 |
| Flexural Stress (23°C) | 200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 32 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 5.2 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, not annealed | 220 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 115 | °C | ISO 75-2/C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 130 - 140 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 20.0 - 30.0 | °C | |
| Rear Temperature | 290 - 300 | °C | |
| Middle Temperature | 310 - 320 | °C | |
| Front Temperature | 330 - 340 | °C | |
| Nozzle Temperature | 310 - 330 | °C | |
| Processing (Melt) Temp | 330 - 340 | °C | |
| Mold Temperature | 140 - 160 | °C | |
| Injection Pressure | 50.0 - 100 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 30.0 - 70.0 | MPa | |
| Back Pressure | 0.00 - 3.00 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 330 to 340°CZone 4 Temperature: 330 to 340°CFeed Temperature: 60 to 80°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1000 TFE 5 HB | RTP Company | PBT | RTP |
| Alpha PVC GW 3026 NAT.LCF | AlphaGary | PVC, Unspecified | Alpha PVC |
| Cawiton® MT970 | Wittenburg B.V. | SEBS | Cawiton® |
| ExxonMobil™ LDPE LD 503.LP | ExxonMobil Chemical | LDPE | ExxonMobil™ LDPE |
| Petrothene® NA960083 | LyondellBasell Industries | LDPE | Petrothene® |