| Exceed™ XP 8318ML is an eXtreme Performance copolymer that offers step-out toughness, high flex-crack resistance and increased output with excellent bubble stability for a range of blown film applications. Exceed™ XP 8318ML - when eXtreme Performance matters. |
| General Information | |
|---|---|
| Additive |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| 1% secant, MD | 193 | MPa | ASTM D882 |
| 1% secant, TD | 231 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 9.70 | MPa | ASTM D882 |
| TD : Yield | 10.0 | MPa | ASTM D882 |
| MD : Fracture | 64.0 | MPa | ASTM D882 |
| TD : Fracture | 51.9 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 370 | % | ASTM D882 |
| TD : Fracture | 660 | % | ASTM D882 |
| Dart Drop Impact | 670 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 370 | g | ASTM D1922 |
| TD | 470 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 20 | ASTM D2457 | |
| Haze | > 30 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Globalene® PT101N | Lee Chang Yung Chemical Industry Corp. | PP Homopolymer | Globalene® |
| Jackdaw ABS/PC FX10BK6455 | Jackdaw Polymers | PC+ABS | Jackdaw ABS/PC |
| PermaStat® 200 FR | RTP Company | Nylon 66 | PermaStat® |
| PLUSTEK PB202G50BK39 | Polyram Ram-On Industries | Nylon 6 | PLUSTEK |
| Celanex® 5214 | Celanese Corporation | PBT | Celanex® |