LNP™ KONDUIT™ PX13322 compound
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ KONDUIT™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gpgpLh_LNP-KONDUIT-PX13322-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Thermally conductive mineral filled PA6 FR compounding |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.69 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.54 | % | |
| Across Flow : 24 hr | 0.57 | % | |
| Water Absorption (23°C, 24 hr) | 0.060 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 13700 | MPa | ASTM D638 |
| -- | 13000 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 77.0 | MPa | ASTM D638 |
| Break | 78.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 0.70 | % | ASTM D638 |
| Break | 0.80 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 11000 | MPa | ASTM D790 |
| -- 5 | 12000 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 128 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 127 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 21 | J/m | ASTM D256 |
| 23°C 7 | 3.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 240 | J/m | ASTM D4812 |
| 23°C 8 | 17 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 205 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 204 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 6.40 mm | 174 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 162 | °C | ISO 75-2/Af |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 3.1E-5 | cm/cm/°C | |
| Flow : 40 to 120°C | 2.4E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 4.8E-5 | cm/cm/°C | |
| Transverse : 40 to 120°C | 5.3E-5 | cm/cm/°C | |
| Thermal Conductivity | |||
| -- 11 | 2.0 | W/m/K | ASTM E1461 |
| -- 12 | 3.4 | W/m/K | ASTM E1461 |
| -- 13 | 1.0 | W/m/K | ISO 22007-2 |
| -- 14 | 3.3 | W/m/K | ISO 22007-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | ASTM D257 |
| Dielectric Strength (1.00 mm, in Oil) | > 10 | kV/mm | ASTM D149 |
| Dielectric Constant (1.10 GHz) | 4.86 | ASTM ES7-83 | |
| Dissipation Factor (1.10 GHz) | 0.010 | ASTM ES7-83 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 1 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index (1.00 to 3.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 800 | °C | |
| 3.00 mm | 850 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 260 to 275 | °C | |
| Middle Temperature | 270 to 290 | °C | |
| Front Temperature | 270 to 290 | °C | |
| Processing (Melt) Temp | 270 to 295 | °C | |
| Mold Temperature | 85.0 to 100 | °C | |
| Back Pressure | 0.200 to 0.300 | MPa | |
| Screw Speed | 20 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| 11 . | through-plane, 10*10*3mm sample |
| 12 . | in-plane, ø25*0.4mm disc |
| 13 . | through-plane, 60*60*3mm plaque |
| 14 . | in-plane, 60*60*3mm plaque |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MELOPAS® MF 152 | RASCHIG GmbH | Mel Formald | MELOPAS® |
| Yanshan PE LD117 | SINOPEC Beijing Yanshan Petrochemical | LDPE | Yanshan PE |
| INLUBE POMHTF20 | Infinity LTL Engineered Compounds | Acetal (POM) Homopolymer | INLUBE |
| PHOENIX™ 2851 | Phon Tech Industrial Company | SEBS | PHOENIX™ |
| Sumiliteresin® PR-50099 I | SBHPP | Phenolic | Sumiliteresin® |