Retpol® 1085 HS 70104
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | PolyPacific Pty. Ltd. |
| Trademark: | Retpol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ikNiYt_Retpol-1085-HS-70104.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Corton 1085 HS 70104 is a 40% talc filled homopolymer polypropylene compound. It is a high flow injection moulding grade developed for rigid components and is stabilized to meet long term automotive heat ageing requirements. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 19 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.70 to 0.90 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 3.00 mm) | 92 | ASTM D785 | |
| Durometer Hardness | ASTM D2240 | ||
| Shore D, 3.00 mm | 79 | ||
| Shore D, 15 sec, 3.00 mm | 71 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.00 mm) | 28.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.00 mm) | 9.0 | % | ASTM D638 |
| Flexural Modulus (3.00 mm) | 3950 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.00 mm) | 20 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.00 mm) | 210 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.00 mm | 130 | °C | |
| 1.8 MPa, Unannealed, 3.00 mm | 77.0 | °C | |
| CLTE - Flow (-30 to 30°C, 3.00 mm) | 6.0E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Regrind | 10 | % | |
| Processing (Melt) Temp | 200 to 260 | °C | |
| Mold Temperature | 20.0 to 60.0 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMTOUGH RZ310G6 | Polyram Ram-On Industries | PC | RAMTOUGH |
| Network Polymers Polyester NPP 60-2008 PETG | Network Polymers, Inc. | PETG | Network Polymers Polyester |
| AKROMID® B3 GK 30 black (1827) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| LNP™ LUBRICOMP™ RX05495 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |
| ESTOPLAST XU 150NN03 | Ester Industries Ltd. | Nylon 6 | ESTOPLAST XU |