Radilon® A RV300W 3002 NER 5444
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Radici Plastics |
| Trademark: | Radilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gpGzuX_Radilon-A-RV300W-3002-NER-5444.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PA66 30% glass fiber reinforced injection moulding grade. Heat stabilized. Black colour. Suitable for parts requiring high stiffness, good mechanical resistance and excellent heat ageing properties retention. ISO 1043 : PA66-T GF30 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.35 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C, 2.00 mm | 6.2 | -- | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 1.6 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9900 | 7500 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 180 | 145 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 3.0 | 6.0 | % | ISO 527-2/1A/5 |
| Flexural Modulus 1 | 9400 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 260 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | 13 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 65 | 90 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 240 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 250 | -- | °C | ISO 306/B50 |
| Melting Temperature 3 | 260 | -- | °C | ISO 11357 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | 0.0 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 700 | -- | °C | IEC 60695-2-12 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 80.0 | °C | |
| Drying Time - Desiccant Dryer | 2.0 to 4.0 | hr | |
| Dew Point - Desiccant Dryer | < -20.0 | °C | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sicoklar UG35 | Ravago Group | PC | Sicoklar |
| Starex HF-0660I | SAMSUNG SDI CO., LTD. | ABS | Starex |
| XANTAR® MX 1000 | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| Nordbak High Temp. Pneu Wear | Loctite® | Epoxy | Nordbak |
| FERREX® GPP20CS14UL-BK | Ferro Corporation | PP Copolymer | FERREX® |