Order Products : sales@su-jiao.com
UBE Nylon 1015GNKF
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | UBE Industries, Ltd. |
| Trademark: | UBE Nylon |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ghxGmd_UBE-Nylon-1015GNKF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Reinforced with glass fiber, heat stabilized, high flow, good welding |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Part Marking Code |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.36 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow | 0.70 | % | |
| Flow | 0.20 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.8 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9900 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 190 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.3 | % | ISO 527-2 |
| Flexural Modulus | 9800 | MPa | ISO 178 |
| Flexural Stress | 290 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 12 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 205 | °C | ISO 75-2/A |
| CLTE - Flow | 2.5E-5 | cm/cm/°C | ISO 11359-2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenite™ Propionate 371A2R30012 Natural, Trsp | Eastman Chemical Company | CAP | Tenite™ Propionate |
| EXTEM™ VH1003F resin | SABIC Innovative Plastics Asia Pacific | PEI | EXTEM™ |
| LIHAN® B801 | Nanjing Lihan Chemical Co., Ltd. | Nylon 6 | LIHAN® |
| Sylvin 9812-65 Brown 7418 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Durethan® AKV 35 CX H2.0 900876 | LANXESS Asia/Pacific | Nylon 66 | Durethan® |