NANCAR® 1051M50 is a high acrylonitrile butadiene copolymer with excellent oil resistance. It is polymerized at low temperature and contains sufficient antioxidant for normal aging conditions. Its low Mooney viscosity makes for good flowability and processability. NANCAR® 1051M50, closely similar to NANCAR® 1051, provides good processing and building tack. It is suggested for use in molded goods, friction stock and similar applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Mooney Viscosity | ASTM D1646 | ||
| ML 1+4, 100°C 1 | 85 | MU | |
| ML 1+4, 100°C | 50 | MU | |
| Acrylonitrile Content - Bound | 41.0 | % | Internal Method |
| Stabilizer | Non-staining |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Loss | 0.70 | % | ASTM D5688 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | |||
| Shore A, 5 sec 2 | 75 | ASTM D2240 | |
| Shore A, 5 sec 3 | 74 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 300% Strain 4 | 12.2 | MPa | |
| 300% Strain 5 | 11.1 | MPa | |
| 300% Strain 6 | 9.00 | MPa | |
| Tensile Strength | ASTM D412 | ||
| Yield 7 | 26.1 | MPa | |
| Yield 8 | 26.0 | MPa | |
| Yield 9 | 25.9 | MPa | |
| Tensile Elongation | ASTM D412 | ||
| Break 10 | 570 | % | |
| Break 11 | 610 | % | |
| Break 12 | 690 | % |
| Note Message | |
|---|---|
| 1 . | Uncured |
| 2 . | CURED @150°C for 60 mins |
| 3 . | CURED @150°C for 40 mins |
| 4 . | CURED @150°C for 60 mins |
| 5 . | CURED @150°C for 40 mins |
| 6 . | CURED @150°C for 20 mins |
| 7 . | CURED @150°C for 60 mins |
| 8 . | CURED @150°C for 40 mins |
| 9 . | CURED @150°C for 20 mins |
| 10 . | CURED @150°C for 60 mins |
| 11 . | CURED @150°C for 40 mins |
| 12 . | CURED @150°C for 20 mins |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| tefanyl® VR VRGR 903 | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Rigid | tefanyl® VR |
| Elastron® V V601.A60.B | Elastron USA, Inc. | TPV | Elastron® V |
| Huafon JF-HSY-9540 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| POLYFLON™ M-392 | Daikin Fluorochemicals (China) Co., Ltd. | PTFE | POLYFLON™ |
| Sylvin 9777-95 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |