SNOLEN® EF 3.3/54
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | JSC Gazprom neftekhim Salavat |
| Trademark: | SNOLEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | maKOGw_SNOLEN-EF-3-3-54.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CHARACTERISTIC PROPERTIES Good environmental stress cracking resistance. MAJOR APPLICATIONS Crops packing. Packing films and sheets. A multilayer film component. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.950 to 0.954 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/21.6 kg | 55 to 65 | g/10 min | |
| 190°C/5.0 kg | 2.5 to 3.3 | g/10 min | |
| Environmental Stress-Cracking Resistance 1(80°C, 2% Arkopal) | 8.00 | hr | ISO 16770 |
| Melt Flow Ratio | 17.0 to 25.0 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Elmendorf Tear Strength | |||
| MD | 458.9 | g/2.5 cm | |
| TD | 4920.1 | g/2.5 cm |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 61 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Secant (23°C) | 1050 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 25.0 | MPa | |
| Break | 30.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 10 | % | |
| Break | > 1000 | % |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Recommended / Available | 20 to 80µm | ||
| Tensile Stress | ISO 527-3/50 | ||
| MD : Break | 41.0 | MPa | |
| TD : Break | 26.0 | MPa | |
| Tensile Elongation - MD (Break) | 490 | % | ISO 527-3/50 |
| Dart Drop Impact | 30 | g | ASTM D1709 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -80.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 73.0 | °C | ISO 306/B50 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | @ 3.5 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene T10P102-00EG | RheTech, Inc. | PP, Unspecified | RheTech Polypropylene |
| UBE Nylon PAE1201U | UBE America, Inc. | Nylon 12 Elast | UBE Nylon |
| NEFTEKHIM PP 8348S (EPH31RA) | Nizhnekamskneftekhim Inc. | PP Copolymer | NEFTEKHIM PP |
| Hanwha Total PP TB62R | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| Kumho KNB 3445G | Korea Kumho Petrochemical Co., Ltd. | NBR | Kumho KNB |