PALBLEND® R FR 0

Category:	PC+ABS , Polycarbonate + ABS
Manufacturer:	pal plast GmbH
Trademark:	PALBLEND®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	gZsSdg_PALBLEND-R-FR-0.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
PALBLEND®R FR 0 is a polycarbonate acrylonitrile butadiene styrene (PC ABS) product,. It is available in Europe. Typical application areas are: electrical/electronic applications. Features include: flame retardant/rated flame Flame Retardant Good UV resistance Halogen-free

General Information
Additive	Flame retardancy
Features	Good UV resistance Halogen-free Flame retardancy
Uses	Electrical/Electronic Applications
Forms	Particle

Physical	Nominal Value	Unit	Test Method
Density	1.16	g/cm³	ISO 1183
Water Absorption			ISO 62
Saturated, 23°C	0.60	%	ISO 62
Equilibrium, 23°C, 50% RH	0.18	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	2550	MPa	ISO 527-2/1A/1
Tensile Stress (Yield, 23°C)	57.5	MPa	ISO 527-2/1A/50
Tensile Strain (Yield, 23°C)	4.0	%	ISO 527-2/1A/50
Nominal Tensile Strain at Break (23°C)	50	%	ISO 527-2/1A/50

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	86.5	°C	ISO 306/B50

Electrical	Nominal Value	Unit	Test Method
Comparative Tracking Index (Solution A)	300	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating (1.60 mm)	V-0		UL 94

Additional Information
Tensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 2400 to 2700 MPaTensile Stress at Yield, ISO 527, 23°C, 50 mm/min, Type A: 55 to 60 MPaTensile Strain at Yield, ISO 527, 23°C, 50 mm/min, Type A: 3 to 5 %Nominal Tensile Strain at Break, ISO 527, 23°C, 50 mm/min, Type A: >50 %Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 85 to 88 °CDensity, ISO 1183: 1.15 to 1.17 g/cm³Water Absorption, ISO 62, 23°C, Saturation: 0.5 to 0.7 %Moisture Absorption, ISO 62, 23°C, 50% RH: 0.15 to 0.2 %

Additional Information

Tensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 2400 to 2700 MPaTensile Stress at Yield, ISO 527, 23°C, 50 mm/min, Type A: 55 to 60 MPaTensile Strain at Yield, ISO 527, 23°C, 50 mm/min, Type A: 3 to 5 %Nominal Tensile Strain at Break, ISO 527, 23°C, 50 mm/min, Type A: >50 %Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 85 to 88 °CDensity, ISO 1183: 1.15 to 1.17 g/cm³Water Absorption, ISO 62, 23°C, Saturation: 0.5 to 0.7 %Moisture Absorption, ISO 62, 23°C, 50% RH: 0.15 to 0.2 %

Resin Grade	Manufacturer	Category	Trademark
Teldene® H25FBA	National Petrochemical Industries Company (NATPET)	PP Homopolymer	Teldene®
MOSTEN TB 002	UNIPETROL RPA	PP Homopolymer	MOSTEN
TOTAL Polyethylene HDPE 8183	TOTAL Refining & Chemicals	HDPE, MMW	TOTAL Polyethylene
TOTAL Polyethylene HDPE XT10 N	TOTAL Refining & Chemicals	HDPE, HMW	TOTAL Polyethylene
DOW™ HDPE NG7000	The Dow Chemical Company	HDPE	DOW™ HDPE